Furan-2,5-dicarboxylic acid (FDCA) is a widely advocated renewable substitute for terephthalic acid (TA). Preparation of high molecular weight FDCA based polyesters by an industrially common combination of melt polymerization and subsequent solid state post condensation is described. Ultimately, poly(ethylene 2,5-furanoate) (PEF) with absolute M n 5 83,000 g mol 21 is obtained, determined by triple detection Size Exclusion Chromatography. The bulk polymer properties of FDCA based polyesters, necessary to evaluate their industrial potential were determined the Young's modulus of PEF is determined to be 2450 6 220 MPa and the maximum stress 35 6 8 MPa. The influence of crystallinity on the mechanical properties as function of temperature was determined by dynamic mechanical thermal analysis. A detailed differential scanning calorimetry study on the crystallization behavior of high molecular weight PEF allowed to calculate the equilibrium melting temperature (T m 0 ) of 239.3 and 239.7 C for the first and second melting peak, respectively. V C 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 4191-4199

In this study we present the application of different isomers of furandicarboxylic acid, or FDCA, obtained from agro-residues, in polyester synthesis. New polyesters based on 2,4-FDCA and 3,4-FDCA isomers with (linear) diols were thoroughly characterised and compared with their as-synthesised 2,5-FDCA analogues. All polymers were obtained by melt polycondensation of linear diols with FDCA dimethyl esters and exhibit molecular weights in the range M w = 34 000-65 000 and polydispersities close to 2.0. Thermogravimetric analysis (TGA) of the new polyesters shows that they have comparable or even higher thermal stability compared to the 2,5-FDCA polyesters. Interestingly, the glass-transition temperatures (T g ) of 2,4-FDCA derived polyesters are similar to those of the 2,5-FDCA isomers. Both differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) analyses showed that 2,4-PEF is amorphous, while 2,5-PEF and 3,4-PEF are semi-crystalline materials. † Electronic supplementary information (ESI) available: 1 H and 13 C NMR spectra, TGA traces, DSC curves and WAXD profiles of all the polyesters. SeeThis journal is

No abstract