The plasticizers used in this study were synthesized from renewable raw materials using succinic acid, oleic acid, and propylene glycol. Four environmentally friendly plasticizer samples were obtained; their chemical structures and compositions were confirmed by gas chromatography (GC) and infrared spectroscopy (FT–IR) analyses, and their physicochemical properties and thermal stability (TGA analysis) were investigated. The obtained ester mixtures were used as poly(vinyl chloride) (PVC) plasticizers and their plasticization efficiency was determined in comparison to traditional, commercially available phthalate plasticizers, such as DEHP (di(2-ethylhexyl phthalate) and DINP (diisononyl phthalate). Mechanical properties and migration resistance were determined for soft PVC with the use of three concentrations of plasticizers (40 PHR, 50 PHR, and 60 PHR). It was observed that the obtained plasticizers exhibited the same plasticization efficiency and were characterized with good mechanical and physical properties in comparison to commercial plasticizers. The tensile strength was approx. 19 MPa, while the elongation at break was approx. 250% for all tested plasticizers at a concentration of 50 PHR. Furthermore, plasticizer migration studies showed that the synthesized plasticizers had excellent resistance to plasticizer leaching. The best migration test result obtained was 70% lower than that for DEHP or DINP. The ester mixture that was found to be the most favorable plasticizer was characterized by good thermal and thermo-oxidative stability (5% weight loss temperature: 227.8 °C in air and 261.1 °C in nitrogen). The results of the research clearly indicate that the synthesized esters can provide a green alternative to toxic phthalate plasticizers.
One of the major objectives of food industry is to develop low-cost biodegradable food packaging films with optimal physicochemical properties, allowing for their large-scale production and providing a variety of applications. To meet the expectations of food industry, we have fabricated a series of solution-cast films based on common biodegradable polysaccharides (starch, chitosan and alginate) to be used in food packaging applications. Selected biopolymers were modified by the addition of glycerol and oxidized sucrose (starch), glycerol (chitosan), and glycerol and calcium chloride (alginate), as well as being used to form blends (starch/chitosan and starch/alginate, respectively). A chestnut extract was used to provide antibacterial properties to the preformed materials. The results of our studies showed that each modification reduced the hydrophilic nature of the polymers, making them more suitable for food packaging applications. In addition, all films exhibited much higher barrier properties to oxygen and carbon dioxide than commercially available films, such as polylactic acid, as well as exhibiting antimicrobial properties against model Gram-negative and Gram-positive bacteria (Escherichia coli and Staphylococcus epidermidis, respectively), as well as yeast (Candida albicans).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.