The presence of a second phase in Al-Cu-MG alloys, with various sizes and supersaturation-solid-solubility, which can be changed by pre-heat-treatment, could have remarkable influence on hot workability and mechanical performance. In the present work, a continuously cast 2024 Al alloy was homogenized and then subjected to hot compression and continuous extrusion (Conform) along with the initial as-cast alloy. The results showed that the 2024 Al alloy specimen with pre-heat treatment had a higher resistance to deformation and dynamic recovery (DRV) during hot compression process compared with the as-cast sample. Meanwhile, dynamic recrystallization (DRX) was advanced in the pre-heat-treated sample. After the Conform Process, the pre-heat-treated sample also attained better mechanical properties without additional solid solution treatment. The higher supersaturation solid solubility and dispersoids generated during pre-heat treatment was proved to play a key role in restricting boundary migration, tangling dislocation motion and promoting the precipitation of S phase, which raised resistance to DRV and plastic deformation and enhanced the mechanical properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.