NaCl ceramics were prepared by room‐temperature cold sintering using moistened NaCl powder with 4 wt% water and dry pressing using dehydrated powder. When the applied uniaxial pressure is low, the relative density of dry‐pressed NaCl ceramic is significantly lower than that of cold‐sintered ceramic, while the former is 98.5%‐99.3% and much higher than the latter (94.3%‐94.6%) for high applied pressure of 200‐300 MPa. The uniaxial pressure‐induced plastic deformation dominates the densification of dry‐pressed NaCl ceramic, and also plays a role during cold sintering as well as the dissolution‐precipitation process. The lower density of cold‐sintered NaCl ceramic under high applied pressure is attributed to the trapped water in ceramic body during cold sintering. Besides, the presence of water always promotes the microstructural homogeneity, which is responsible for the much higher Qf value of cold‐sintered NaCl ceramic. The optimal microwave dielectric properties with εr = 5.55, Qf = 49 600 GHz, and τf = −173 ppm/°C are obtained in cold‐sintered NaCl ceramic under the applied pressure of 300 MPa, indicating that it is a promising candidate as a microwave dielectric material.
• PBO of IIA, CIA and IAA is effective in placenta accreta. • PBO of CIA and IAA is more effective. • PBO could independently predict less EBL. • Accreta depth was an independent risk factor for EBL.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.