A shell of P123-templated CeMgAl-LDO was distributed in transverse and longitudinal directions on spheres of SiO2. The composites displayed high catalytic activity in the synthesis of propylene glycol methyl ether.
The mechanical properties of molded pulp materials are the basis of the structural optimum design of molded pulp products. Therefore, the correlations between Poisson’s ratio and fiber structure, molding process, and thickness were found for materials including wood pulp, bamboo pulp, sugarcane pulp, white mixed pulp, black mixed pulp, recycled corrugated board pulp, and recycled newspaper pulp by the uniaxial tensile test and digital image correlation method. The fiber structures of the selected molded pulp materials were investigated by scanning electron microscopy. The results revealed Poisson’s ratios of wood pulp, bamboo pulp, sugarcane pulp, white mixed pulp, black mixed pulp, recycled corrugated board pulp, and recycled newspaper pulp to be 0.169, 0.108, 0.202, 0.120, 0.166, 0.098, and 0.044, respectively. Microstructural investigation further revealed that Poisson’s ratios of molded pulp materials were related to the fiber structure and drying method. The pulp material dried outside mold under lower pressure and temperature had a smaller Poisson’s ratio, while that dried inside mold under higher pressure and temperature had a larger Poisson’s ratio. The layered phenomenon of the molded pulp materials was also found by scanning electron microscopy images: the outer layer was denser than the inner layer. These results can provide guidance for the numerical simulation analysis and optimal design of molded pulp products.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.