Plasmonic Au nanoparticles embedded in LiNbO3 crystals as efficient saturable absorbers to realize 74.1 ps mode‐locked laser pulse generation at 1 µm are reported. The system is fabricated by Au ion implantation and subsequent annealing, a well‐developed chip technology. The strong optical absorption band peaking at 640 nm is observed due to the localized surface plasmon resonance. Z‐scan investigation shows that the LiNbO3 crystals with embedded Au nanoparticles possess ultrafast saturable absorption properties at near‐infrared 1 µm wavelength. With this feature the Au nanoparticles embedded LiNbO3 wafer is applied as saturable absorber into a laser‐written Nd:YVO4 waveguide platform. Stable laser pulses at 1064 nm based on an efficient passive Q‐switched mode‐locking process, reaching a fundamental repetition rate of 6.4 GHz and a pulse duration of 74.1 ps, are obtained. Since LiNbO3 has broadband applications in various optical systems, this work opens the way to develop intriguing devices in LiNbO3‐based photonic circuits by using embedded metallic nanoparticles.
We report on the synthesis of embedded gold (Au) nanoparticles (NPs) in Nd:YAG single crystals using ion implantation and subsequent thermal annealing. Both linear and nonlinear absorption of the Nd:YAG crystals have been enhanced significantly due to the embedded Au NPs, which is induced by the surface plasmon resonance (SPR) effect in the visible light wavelength band. Particularly, through a typical Z-scan system excited by a femtosecond laser at 515 nm within the SPR band, the nonlinear absorption coefficients of crystals with Au NPs have been observed to be nearly 5 orders of magnitude larger than that without Au NPs. This giant enhancement of nonlinear absorption properties is correlated with the saturable absorption (SA) effect, which is the basis of passive Q-switching or mode-locking for pulsed laser generation. In addition, the linear and nonlinear absorption enhancement could be tailored by varying the fluence of implanted Au ions, corresponding to the NP size and concentration modulation. Finally, the Nd:YAG wafer with embedded Au NPs has been applied as a saturable absorber in a Pr:LuLiF crystal laser cavity, and efficient pulsed laser generation at 639 nm has been realized, which presents superior performance to the MoS saturable absorber based system. This work opens an avenue to enhance and modulate the nonlinearities of dielectrics by embedding plasmonic Au NPs for efficient pulsed laser operation.
The femtosecond laser micromachining of transparent optical materials offers a powerful and feasible solution to fabricate versatile photonic components towards diverse applications. In this work, we report on a new design and fabrication of ridge waveguides in LiNbO3 crystal operating at the mid-infrared (MIR) band by all-femtosecond-laser microfabrication. The ridges consist of laser-ablated sidewalls and laser-written bottom low-index cladding tracks, which are constructed for horizontal and longitudinal light confinement, respectively. The ridge waveguides are found to support good guidance at wavelength of 4 μm. By applying this configuration, Y-branch waveguiding structures (1 × 2 beam splitters) have been produced, which reach splitting ratios of ∼1:1 at 4 μm. This work paves a simple and feasible way to construct novel ridge waveguide devices in dielectrics through all-femtosecond-laser micro-processing.
Integrated photonic devices with beam splitting function are intriguing for a broad range of photonic applications. Through optical-lattice-like cladding waveguide structures fabricated by direct femtosecond laser writing, the light propagation can be engineered via the track-confined refractive index profiles, achieving tailored output beam distributions. In this work, we report on the fabrication of 3D laser-written optical-lattice-like structures in a nonlinear KTP crystal to implement 1 × 4 beam splitting. Second harmonic generation (SHG) of green light through these nonlinear waveguide beam splitter structures provides the capability for the compact visible laser emitting devices. With Type II phase matching of the fundamental wavelength (@ 1064 nm) to second harmonic waves (@ 532 nm), the frequency doubling has been achieved through this three-dimensional beam splitter. Under 1064-nm continuous-wave fundamental-wavelength pump beam, guided-wave SHG at 532 nm are measured with the maximum power of 0.65 mW and 0.48 mW for waveguide splitters (0.67 mW and 0.51 mW for corresponding straight channel waveguides), corresponding to a SH conversion efficiency of approximately ~14.3%/W and 13.9%/W (11.2%/W, 11.3%/W for corresponding straight channel waveguides), respectively. This work paves a way to fabricate compact integrated nonlinear photonic devices in a single chip with beam dividing functions.
Low-loss depressed cladding waveguides have been produced in Nd:YAP laser crystal by using direct femtosecond laser writing. Under optical pump at 812 nm at room temperature, continuous-wave simultaneous dual-wavelength laser oscillations at 1064 and 1079 nm, both along TM polarization, have been realized in the waveguiding structures. It has been found that, with the variation of pump polarization, the intensity ratio of 1064 and 1079 nm emissions varies periodically, while the polarization of output dual-wavelength laser remains unchanged. The maximum output power achieved for the Nd:YAP waveguide lasers is ∼200 mW with a slope efficiency of 33.4%.
We report on the fabrication of optical lattice-like waveguide structures in an Nd:YAP laser crystal by using direct femtosecond laser writing. With periodically arrayed laser-induced tracks, the waveguiding cores can be located in either the regions between the neighbored tracks or the central zone surrounded by a number of tracks as outer cladding. The polarization of the femtosecond laser pulses for the inscription has been found to play a critical role in the anisotropic guiding behaviors of the structures. The confocal photoluminescence investigations reveal different stress-induced modifications of the structures inscribed by different polarization of the femtosecond laser beam, which are considered to be responsible for the refractive index changes of the structures. Under optical pump at 808 nm, efficient waveguide lasing at ∼1 μm wavelength has been realized from the optical lattice-like structure, which exhibits potential applications as novel miniature light sources.
Efficient radiative recombination is essential for perovskite luminescence, but the intrinsic radiative recombination rate as a basic material property is challenging to tailor. Here we report an interfacial chemistry strategy to dramatically increase the radiative recombination rate of perovskites. By coating aluminum oxide on the lead halide perovskite, lead–oxygen bonds are formed at the perovskite‐oxide interface, producing the perovskite surface states with a large exciton binding energy and a high localized density of electronic state. The oxide‐bonded perovskite exhibits a ≈500 fold enhanced photoluminescence with a ≈10 fold reduced lifetime, indicating an unprecedented ≈5000 fold increase in the radiative recombination rate. The enormously enhanced radiative recombination promises to significantly promote the perovskite optoelectronic performance.
We report on the fabrication of ring-shaped waveguides operating at the telecommunication band in a cubic BiGeO (BGO) crystal by using technique of femtosecond laser writing. In the regions of laser written tracks in BGO crystal, positive refractive index is induced, resulting in so-called Type I configuration. The modal profiles are within the designed track cladding with ring-shaped geometries, which are analogous to circular optical lattices. The homogenous guidance along both TE and TM polarizations has been obtained at telecommunication wavelength of 1.55 μm. Both straight and S-curved waveguiding structures have been produced with ring-shaped configurations. This work paves the way to fabricate complex photonic networks for telecommunications by using ring-shaped waveguides in compact chips.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.