High-voltage energy-storage devices are quite commonly needed for robots and dielectric elastomers. This paper presents a flexible high-voltage microsupercapacitor (MSC) with a planar in-series architecture for the first time based on laser-induced graphene. The high-voltage devices are capable of supplying output voltages ranging from a few to thousands of volts. The measured capacitances for the 1, 3, and 6 V MSCs were 60.5, 20.7, and 10.0 μF, respectively, under an applied current of 1.0 μA. After the 5000-cycle charge-discharge test, the 6 V MSC retained about 97.8% of the initial capacitance. It also was recorded that the all-solid-state 209 V MSC could achieve a high capacitance of 0.43 μF at a low applied current of 0.2 μA and a capacitance of 0.18 μF even at a high applied current of 5.0 μA. We further demonstrate the robust function of our flexible high-voltage MSCs by using them to power a piezoresistive microsensor (6 V) and a walking robot (>2000 V). Considering the simple, direct, and cost-effective fabrication method of our laser-fabricated flexible high-voltage MSCs, this work paves the way and lays the foundation for high-voltage energy-storage devices.
Fiber shaped supercapacitors are promising candidates for wearable electronics because they are flexible and light-weight. However, a critical challenge of the widespread application of these energy storage devices is their low cell voltages and low energy densities, resulting in limited run-time of the electronics. Here, we demonstrate a 1.5 V high cell voltage and high volumetric energy density asymmetric fiber supercapacitor in aqueous electrolyte. The lightweight (0.24 g cm−3), highly conductive (39 S cm−1), and mechanically robust (221 MPa) graphene fibers were firstly fabricated and then coated by NiCo2S4 nanoparticles (GF/NiCo2S4) via the solvothermal deposition method. The GF/NiCo2S4 display high volumetric capacitance up to 388 F cm−3 at 2 mV s−1 in a three-electrode cell and 300 F cm−3 at 175.7 mA cm−3 (568 mF cm−2 at 0.5 mA cm−2) in a two-electrode cell. The electrochemical characterizations show 1000% higher capacitance of the GF/NiCo2S4 as compared to that of neat graphene fibers. The fabricated device achieves high energy density up to 12.3 mWh cm−3 with a maximum power density of 1600 mW cm−3, outperforming the thin-film lithium battery. Therefore, these supercapacitors are promising for the next generation flexible and wearable electronic devices.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.