a b s t r a c tPolymer electrolyte composite membranes based on poly(1-vinyl-1,2,4-triazole) (PVTRI) and nitrilotri(methyl triphosphonic acid) (TPA) were investigated. PVTRI was produced by free radical polymerization of 1-vinyl-1,2,4-triazole. The polymer PVTRI was doped with TPA at various molar ratios x ¼ 0.125, x ¼ 0.25, and x ¼ 0.5. The proton transfer from TPA to the triazole rings was proved with Fourier-transform infrared spectroscopy (FT-IR). Thermogravimetry (TG) analysis showed that the samples are thermally stable up to approximately 250 1C. DSC results illustrated the homogeneity of the materials as well as the softening effect of the dopant. Cyclic voltammetry results illustrated that the electrochemical stability domain of the dopant extends over 1.5 V. The maximum proton conductivity has been measured for PVTRITPA-0.25 as 8.5 Â 10 À 4 S cm À 1 at 150 1C.
Abstract. In this work, acid-base complex pair polymer electrolyte membranes on sulfonated polysulfone with 1H-benzotriazole were investigated. Polysulfone was sulfonated in 1,2-dichloroethane using the homogeneous method with trimethylsilyl chlorosulfonate as sulfonating agent. The monomer mole ratio between polysulfone and trimethysilyl chlorosulfonate was 1:1.5. The sulfonated polysulfone was added with 1H-benzotriazole at mole ratios of x = 0.5 and x =1. The proton transfer from 1H-benzotriazole to the sulfonated polysulfone was measured using FTIR. Thermo-gravimetry analysis showed that the samples were thermally stable up to approximately 250°C and the maximum proton conductivity was found to be 3.34 x 10 -4 S cm -1 at 150°C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.