Electrospinning has been widely used to prepare polymer fibers with diameters ranging from a few nanometers to micrometers. While most studies focus on controlling the sizes and morphologies of electrospun polymer fibers by changing electrospinning conditions, the effect of post-treatments such as thermal annealing on the properties of electrospun polymer fibers has been less studied. Here, we investigate the effect of thermal annealing on the morphology changes of electrospun polystyrene (PS) fibers on substrates. Different from annealing the fibers in a uniform environment, annealing the fibers on substrates results in a substrate-dependent morphology transformation. When the electrospun PS fibers are annealed on a glass substrate, wetting of the fibers on the glass substrate occurs. When the electrospun PS fibers are annealed on a poly(methyl methacrylate) (PMMA)-coated substrate, a Rayleigh-instability-driven morphology transformation is observed. The polymer fibers transform into hemispherical polymer particles caused by the lower surface tension of PS than that of PMMA and the interfacial tension between PS and PMMA. This transformation process is influenced by the annealing time and temperature. The characteristic time of the transformation process is shorter when the sample is annealed at a higher temperature because of the lower polymer viscosity. The size of the polymer particles fits well with the theoretical prediction, which is dependent on the initial fiber diameter and is independent of the annealing temperature.
We demonstrate a simple route to fabricate hierarchical structures by combining the electrospinning technique and the wetting of porous templates. Poly(methyl methacrylate) (PMMA) fibers are first prepared by electrospinning and are collected on a glass substrate. The PMMA fibers are then brought into contact with an anodic aluminum oxide template. Upon thermal annealing above the glass transition temperature of PMMA, wetting of the polymer chains into the nanopores occurs. After the removal of the AAO template, ordered arrays of nanorods on polymer fibers are obtained. This approach is also applied to polystyrene (PS), and similar structures are obtained. This work provides a promising approach to fabricate hierarchical polymer structures with sizes that can be controlled over the nanoscopic and microscopic length scales.
Electrospinning is a simple and convenient technique to produce polymer fibers with diameters ranging from several nanometers to a few micrometers. Different types of polymer fibers have been prepared by electrospinning for various applications. Among different post-treatment methods of electrospun polymer fibers, the annealing process plays a critical role in controlling the fiber properties. The morphology changes of electrospun polymer fibers under annealing, however, have been little studied. Here we investigate the annealing effect of electrospun poly(methyl methacrylate) (PMMA) fibers and their transformation into PMMA microspheres. PMMA fibers with an average size of 2.39 μm are first prepared by electrospinning a 35 wt% PMMA solution in dimethylformamide. After the electrospun fibers are thermally annealed in ethylene glycol, a non-solvent for PMMA, the surfaces of the fibers undulate and transform into microspheres driven by the Rayleigh instability. The driving force of the transformation process is the minimization of the interfacial energy between the polymer fibers and ethylene glycol. The sizes of the microspheres fit well with the theoretical predictions. Longer annealing times are found to be required at lower temperatures to obtain the microspheres.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.