Modified acrylamide-based semi-interpenetrating polymer network (semi-IPN) hydrogel composites were prepared for Congo red (CR) and Bismarck brown Y (BBY) dyes adsorption from aqueous solutions. Adsorption for both dyes was studied in batch mode and results show adsorption highly dependent on concentration, solution pH, and contact time. The prepared hydrogels exhibited a high adsorption capability. Also, the kinetic studies indicated that the adsorption of dyes followed the pseudosecond-order model and was found to match well with the Langmuir isotherm model. Thermodynamic studies showed that the adsorption process was spontaneous and endothermic. The prepared hydrogel composites also exhibit good regeneration efficiency for the four successive adsorption-desorption cycles. Based on these analyses, it can be concluded that these adsorbents be acted as an efficient option for the removal of contaminant dyes from aqueous solutions.
Hydrogels of acrylamide (AM), acrylamide\ 2-acrylamido-2-methyl-1-propane sulphonic acid (AMS), and acrylamide\ 2-acrylamido-2-methyl-1-propane sulphonic acid\graphene oxide (AMSGO) were prepared as adsorbents to remove carcinogenic dyes Congo red (CR) and Bismarck brown Y (BBY) from aqueous solutions. Hydrogels were characterized using FSEM and XRD analyses. For both dyes, the synthesized hydrogels demonstrated high adsorption capability at near-neutral pH. Experimental adsorption data were analyzed using the Langmuir and Freundlich isotherm models. It was found that the Langmuir model was more suitable for the experimental data. Kinetic studies found that the pseudo-second-order model demonstrated the best fitting to the experimental data. In addition, thermodynamic studies suggest that the adsorption process was spontaneous and endothermic. The prepared hydrogels were regenerated and reused in four consecutive cycles and it could be applied to remove anionic dyes from aqueous solutions as an effective adsorbent.
Introduction: Phenolic resins have been in use since the early twentieth century and are considered the first class of synthetic polymers to achieve commercial success, moreover phenolic resins continue to succeed and attract special interest in a large range of industrial applications such as adhesives, paints, and composites; because of their unique physical and chemical properties. Materials and Methods: Prepolymers resol resins (RR, RH, RP, and RC) were synthesized by the reaction of phenolic compounds (resorcinol, hydroquinone, phloroglucinol, and catechol) respectively, with formaldehyde at molar ratio phenol/ formaldehyde 1/1.5, using sodium hydroxide as a catalyst. These resins were characterized by FTIR. The curing reaction of these resins was evaluated using differential scanning calorimetry (DSC), while the thermal stability study was evaluated using thermogravimetric analysis (TGA). Results and Discussion:From the results showing that these prepolymers have different curing temperatures and curing energy, while the TGA study showed that the cured resins have decomposition temperature more than 300 ºC, and char residue at 650 ºC more than 60%. Conclusions: These resol resins have different gel times (8-55) min, and viscosities (435-350) mpa.s. The curing temperature of these resin obtained from DSC curves was (120, 129, 105 and 127 °C), while the thermal behavior of the cured resins obtained from TGA curves showed that these cured resin have two decomposition temperatures and the rate of decomposition in the order of RC < RR< .
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.