This work investigated the influence of the aggregate's aspect ratio on the fracture behavior of a low cement aluminum silicate refractory castable treated at two different temperatures (110 °C and 1000 °C). The aggregates were cylindrical pellets with an aspect ratio of 1, 2, 3 and 4, produced by extruding a mixture of clay and calcined alumina fired at 1600 °C for 4 h to yield mullite (3Al2O3.2SiO2). The behavior of the R-Curve and other relevant fracture parameters were evaluated based on the "Two Parameter Fracture Model" in a three-point flexure test of single-edge straight through notched specimens. The two temperature treatments produced different degrees of matrix-aggregate adhesion. The larger aspect ratio aggregates were found to promote toughening only in the dried condition, at 110 °C, while the specimens fired at 1000 °C for 4 h, regardless of their aggregate aspect ratio, displayed no significant toughening. The best results for fired samples, however, were obtained from specimens containing conventional angular aggregates
O objetivo deste trabalho foi recuperar um resíduo proveniente de pilhas do tipo zinco-carvão para ser utilizado como aditivo em argamassas e concretos, dando assim, uma solução para as pilhas e ao mesmo tempo ajudando a resolver a questão ambiental incluindo-as na indústria brasileira de reciclagem. Desse modo, foi possível caracterizar e avaliar as possibilidades de utilização desse rejeito. Foram coletadas pilhas para serem caracterizadas através de diferentes análises, assim como, densidade real e área específica (BET). Também se utilizou a técnica de difração de raios X, pH e microscopia eletrônica de varredura em conjunto com espectroscopia dispersiva de energia por raios X.
Dynamical Elastic Moduli of the Ti-13Nb-13Zr biomaterial alloy were obtained using the mechanical spectroscopy technique. The sample with heat treatment at 1170K for 30 minutes and water quenched with subsequent aging treatment at 670 K for 3 hours (TNZ + WQ + 670 K/3 h), was characterized through decay of free oscillations of the sample in the flexural vibration mode. The spectra of anelastic relaxation (internal friction and frequency) in the temperature range from 300 K to 625 K not revealed the presence of relaxation process. As shown in the literature, the hcp structure usually does not exhibit any relaxation due to the symmetry of the sites in the crystalline lattice, but if there is some relaxation, this only occurs in special cases such as low concentration of zirconium or saturation of the stoichiometric ratio of oxygen for zirconium. Dynamical elastic modulus obtained for TNZ + WQ + 670 K/3 h alloy was 87 GPa at room temperature, which is higher than the value for Ti-13Nb-13Zr alloy (64 GPa) of the literature. This increment may be related to the change of the proportion of α and β phases. Besides that, the presence of precipitates in the alloy after aging treatment hardens the material and reduces its ductility.
O objetivo deste trabalho consistiu em um estudo da influência de dois tipos diferentes de cimento Portland na propriedade fluência em concretos, em equipamento específico, uma propriedade viscoelástica que se origina na pasta endurecida de cimento e presume-se que esteja relacionada principalmente à remoção da água adsorvida. As causas da fluência no concreto são complexas. Normalmente concorda-se que, além dos movimentos da umidade, há outras causas que contribuem para o fenômeno de fluência. A não-linearidade da relação tensão-deformação no concreto, especialmente em níveis de tensão maiores do que 30 a 40 por cento da última tensão, mostra claramente a contribuição das microfissuras da zona de transição à fluência, um fenômeno bem conhecido nas engenharias civil e materiais. A técnica de formação de uma microestrutura controlada vem sendo apontada como uma promissora alternativa para o entendimento do mecanismo de fluência. A avaliação do estudo bibliográfico procurou apontar os principais parâmetros e variáveis envolvidas nesta propriedade, de maneira a incentivar o seu desenvolvimento e pesquisa.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.