In this work, an electroless CoWP film deposited on a silicon substrate as a diffusion barrier for electroless Cu and silicon has been studied. Four different Cu 120 nm/CoWP/Si stacked samples with 30, 60, 75, and 100 nm electroless CoWP films were prepared and annealed in a rapid thermal annealing (RTA) furnace at 300°C to 800°C for 5 min. The failure behavior of the electroless CoWP film in the Cu/CoWP/Si sample and the effect of CoWP film thickness on the diffusion barrier properties have been investigated by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and sheet resistance measurements. The composition of the electroless CoWP films was 89.4 at.% Co, 2.4 at.% W, and 8.2 at.% P, as determined by energy dispersive X-ray spectrometer (EDS). A 30 nm electroless CoWP film can prevent copper penetration up to 500°C, and a 75 nm electroless CoWP film can survive at least up to 600°C. Therefore, increasing the thickness of electroless CoWP films effectively increases the failure temperature of the Cu/CoWP/Si samples. The observations of SEM and TEM show that interdiffusion of the copper and cobalt causes the failure of the electroless CoWP diffusion barriers in Cu/CoWP/Si during thermal annealing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.