Urethane dimethacrylate (UDMA), an oligomeric poly(ethylene glycol) extended UDMA (PEG-U) and a blend of UDMA/PEG-U were chosen as model systems for introducing both hydrophobic and hydrophilic segments and a range of compliances in their derived polymers. Experimental composites based on these three resins with amorphous calcium phosphate (ACP) as the filler phase were polymerized and evaluated for mechanical strength and ion release profiles in different aqueous media. Strength of all composites decreased upon immersion in saline (pH = 7.4). Both polymer matrix composition and the pH of the liquid environment strongly affected the ion release kinetics. In saline, the UDMA/PEG-U composite showed a sustained release for at least 350 h. The initially high ion release of the PEG-U composites decreased after 72 h, seemingly due to the mineral re-deposition at the composite surface. Internal conversion from ACP to poorly crystallized apatite could be observed by X-ray diffraction. In various lactic acid (LA) environments (initial pH = 5.1) ion release kinetics was much more complex. In LA medium without thymol and/or carboxymethylcellulose, as a result of unfavorable changes in the internal calcium/phosphate ion stoichiometry, the ion release rate greatly increased but without observable conversion of ACP to apatite.

No abstract

The random clustering of amorphous calcium phosphate (ACP) particles within resin matrices is thought to diminish the strength of their polymerized composites. The objective of this study was to elucidate the effect of ball-milling on the particle size distribution (PSD) of ACP fillers and assess if improved dispersion of milled ACP in methacrylate resin sufficiently enhanced filler/matrix interactions to result in improved biaxial flexure strength (BFS), without compromising the remineralizing potential of the composites. Unmilled and wet-milled zirconia-hybridized ACP (Zr-ACP) fillers were characterized by PSD analysis, X-ray diffraction, thermogravimetric and chemical analysis, infrared spectroscopy, and scanning electron microscopy. Composite specimens made from a photoactivated, ternary methacrylate resin admixed with a mass fraction of 40% of un-milled or milled Zr-ACP were evaluated for the BFS (dry and wet) and for the release of calcium and phosphate ions into saline solutions. While having no apparent effect on the structure, composition, and morphology/topology of the fillers, milling significantly reduced the average size of Zr-ACP particulates (median diameter, d m ‫؍‬ 0.9 ؎ 0.2 m) and the spread of their PSD. Better dispersion of milled Zr-ACP in the resins resulted in the improved BFS of the composites, even after aqueous soaking, and also gave a satisfactory ion release profile. The demonstrated improvement in the mechanical stability of anti-demineralizing/remineralizing ACP composites based on milled Zr-ACP filler may be beneficial in potentially extending their dental utility.

This study explores how substituting a new high molecular mass oligomeric poly(ethylene glycol) extended urethane dimethacrylate (PEG-U) for 2-hydroxyethyl methacrylate (HEMA) in photoactivated urethane dimethacrylate (UDMA) resins affects degree of vinyl conversion (DC), polymerization shrinkage (PS), stress development (PSSD) and biaxial flexure strength (BFS) of their amorphous calcium phosphate (ACP) composites. The composites were prepared from four types of resins (UDMA, PEG-U, UDMA/HEMA and UDMA/PEG-U) and zirconia-hybridized ACP. Introducing PEG-U improved DC while not adversely affecting PS, PSSD and the BFS of composites. This improvement in DC is attributed to the long, more flexible structure between the vinyl groups of PEG-U and its higher molecular mass compared to poly(HEMA). The results imply that PEG-U has the potential to serve as an alternative to HEMA in dental and other biomedical applications.