Depth profile of Helium irradiation effects in reactor pressure vessel (RPV) model material is identified using a nano-indentation technique in order to develop a new methodology to clarify the solute-vacancy interaction. 2 MeV He ion was irradiated in pure iron at room temperature with and without an energy degrator. The indentation hardness was measured by nanoindentation changing the load at 9 levels. Hardening in irradiated materials was clearly observed in all indentation loads as well as the well-known indentation size effect. It was interesting that the significant increase of hardness was recognized at 0.8 μm depth, which is corresponding to the obstacle of deformation at 3˜4 μm depth, that would be the cause of helium implantation. Furthermore, dose effects on 3MeV Si irradiated RPV model materials were confirmed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.