The micro-Wilhelmy method is a well-established method of determining surface tension by measuring the force of withdrawing a tens of microns to millimeters in diameter cylindrical wire or fiber from a liquid. A comparison of insertion force to retraction force can also be used to determine the contact angle with the fiber. Given the limited availability of atomic force microscope (AFM) probes that have long constant diameter tips, force-distance (F-D) curves using probes with standard tapered tips have been difficult to relate to surface tension. In this report, constant diameter metal alloy nanowires (referred to as "nanoneedles") between 7.2 and 67 microm in length and 108 and 1006 nm in diameter were grown on AFM probes. F-D and Q damping AFM measurements of wetting and drag forces made with the probes were compared against standard macroscopic models of these forces on slender cylinders to estimate surface tension, contact angle, meniscus height, evaporation rate, and viscosity. The surface tensions for several low molecular weight liquids that were measured with these probes were between -4.2% and +8.3% of standard reported values. Also, the F-D curves show well-defined stair-step events on insertion and retraction from partial wetting liquids, compared to the continuously growing attractive force of standard tapered AFM probe tips. In the AFM used, the stair-step feature in F-D curves was repeatably monitored for at least 0.5 h (depending on the volatility of the liquid), and this feature was then used to evaluate evaporation rates (as low as 0.30 nm/s) through changes in the surface height of the liquid. A nanoneedle with a step change in diameter at a known distance from its end produced two steps in the F-D curve from which the meniscus height was determined. The step features enable meniscus height to be determined from distance between the steps, as an alternative to calculating the height corresponding to the AFM measured values of surface tension and contact angle. All but one of the eight measurements agreed to within 13%. The constant diameter of the nanoneedle also is used to relate viscous damping of the vibrating cantilever to a macroscopic model of Stokes drag on a long cylinder. Expected increases in drag force with insertion depth and viscosity are observed for several glycerol-water solutions. However, an additional damping term (associated with drag of the meniscus on the sidewalls of the nanoneedle) limits the sensitivity of the measurement of drag force for low-viscosity solutions, while low values of Q limit the sensitivity for high-viscosity solutions. Overall, reasonable correspondence is found between the macroscopic models and the measurements with the nanoneedle-tipped probes. Tighter environmental control of the AFM and treatments of needles to give them more ideal surfaces are expected to improve repeatability and make more evident subtle features that currently appear to be present on the F-D and Q damping curves.
Electrical properties of a chemical sensor constructed from mats of GaN nanowires decorated with gold nanoparticles as a function of exposure to Ar, N2, and methane are presented. The Au nanoparticle decorated nanowires exhibited chemically selective electrical responses. The sensor exhibits a nominal response to Ar and slightly greater response for N2. Upon exposure to methane the conductivity is suppressed by 50% relative to vacuum. The effect is fully reversible and is independent of exposure history. We offer a model by which the change in the current is caused by a change in the depletion depth of the nanowires, the change in the depletion depth being due to an adsorbate induced change in the potential on the gold nanoparticles on the surface of the nanowires.
Chemiresistors were constructed using 3-D silica nanospring mats coated with a contiguous film of ZnO nanocrystals. Chemiresistors with an average ZnO nanocrystal radius <3 nm, or >20 nm, were found to exhibit a relative change in conductance of a factor of 50 upon exposure to a gas flow of 20% O2 and 80% N2 with ∼500 ppm of toluene and an operational temperature of 400 °C. Samples with an average ZnO nanocrystal radius of 15 nm were found to be the most responsive with a relative conductance change of a factor of 1000. The addition of metal nanoparticles (average radius equal to 2.4 nm) onto the surface of the ZnO nanocrystals (average radius equal to 15 nm) produced a relative change in conductance of a factor of 1500. For the optimum conditions (T = 400 °C, grain size ∼15 nm) well-defined spikes in conductance to explosive vapors (TNT, TATP) were obtained for 0.1 ms exposure time at ppb levels.
Chemiresistors (conductometric sensor) were fabricated on the basis of novel nanomaterials—silica nanosprings ALD coated with ZnO. The effects of high temperature and UV illumination on the electronic and gas sensing properties of chemiresistors are reported. For the thermally activated chemiresistors, a discrimination mechanism was developed and an integrated sensor-array for simultaneous real-time resistance scans was built. The integrated sensor response was tested using linear discriminant analysis (LDA). The distinguished electronic signatures of various chemical vapors were obtained at ppm level. It was found that the recovery rate at high temperature drastically increases upon UV illumination. The feasibility study of the activation method by UV illumination at room temperature was conducted.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.