The 304 Stainless Steel (SS304) is severely affected by salt water corrosion due to its high surface wettability. By reducing its surface wettability, its corrosion can be reduced. To achieve this, topographical modification of the steel surface is an effective route. In this work, SS304 flat surfaces were topographically modified into microgrooves (ridge width 250 μm to 500 μm, groove width 200 μm, width ratio = ridge width/groove width >1). Wire cut electrical discharge machining was used to fabricate the microgrooves. Long-term wetting characteristics and long-term corrosion behaviour of flat surface and microgrooves were studied. The influence of the nature of wetting of the tested surfaces on their corrosion behaviour was examined. The sessile drop method and potentiodynamic polarization tests in sodium chloride (3.5 wt. % NaCl) solution (intermittent and continuous exposures for 168 h) were studied to characterize their wetting and corrosion behaviours, respectively. Topographical modification imparted long-term hydrophobicity and, as a consequence, long-term anticorrosion ability of the steel surface. Micropatterning reduced the corrosion rate by two orders of magnitude due to reduction in interfacial contact area with the corrosive fluid via composite wetting, i.e., solid–liquid–air interface. Microgrooves showed corrosion inhibition efficiency ³88%, upon long-term exposure to NaCl solution. By comparing the wetting and corrosion behaviours of the microgrooves with those of the previously studied microgrooves (ridge width/groove width <1), it was found that the surface roughness of their ridges strongly influences their wetting and corrosion properties.
Stainless steel 304 (SS304) experiences corrosion when it is exposed to a saline atmosphere, which attains severity due to its high surface wettability. Topographical modification of metallic surfaces is an effective route to reduce wettability and thereby mitigate liquid-mediated corrosion. In this work, topographical modification of stainless steel 304 flat surface in the form of micropillars was done (pillar width: 100 μm, inter-pillar distance: 100 μm and height: 80 μm). Micropillars were fabricated by a chemical etching process. Wetting and corrosion of the micropillars was studied over long-time duration in comparison with flat surface, before and after intermittent and continuous exposures to saline water for 168 h. Wetting was characterized by measuring the static water contact angle on the test surfaces and their corrosion by electrochemical polarization tests (electrolyte: 3.5 wt.% sodium chloride solution). The relationship between the nature of wetting of the test surfaces and their corrosion was examined. Micropillars showed predominantly composite wetting over a long time, which imparted an effective resistance against corrosion over a long time to the SS304 surface. When compared to the flat surface, the corrosion rates of the micropillars were lower by two orders of magnitude, prior to and also upon long-time contact with the NaCl solution. Micropillars lowered corrosion due to composite wetting, i.e., solid-liquid-air interface that reduced the area that was in contact with the NaCl solution. The efficiency of corrosion inhibition (η) of micropillars was 88% before long-time contact, 84% after intermittent contact, and 77% after continuous contact with NaCl solution. Topographical modification in the form of micropillars that can impart composite wetting is an effective route to induce long-term anticorrosion ability to the SS304 surface.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.