Fuel cells have important applications in recent decades due to high-energy demands, fossil fuel depletions, and environmental pollution throughout world. Pt/Pd nanoparticles/polyoxometalate/ionic liquid (ILs) nanohybrid synthesized for the first time and characterized by transmission electron microscope, scanning electron microscope, X-ray photo electron spectroscopy, energydispersive X-ray spectroscopy and X-ray diffraction method. A cost-effective catalyst has been developed on Pt/Pd nanoparticles/polyoxometalate/ionic liquid nanohybrid. The developed catalyst based on bimetallic nanoparticle demonstrates effective methanol oxidation in comparison with catalysts on monometallic nanoparticle and polyoxometalate/ionic liquid nanohybrid.

No abstract

Hard, tough, lightweight boron-carbide-reactive metal composites, boron-carbide-aluminum composites, are produced. The ultrasonic velocity and attenuation were measured on B 4 C-Al-Ni ceramic-metal composites, which are sintered in the temperature range 500-1200• C, by using the pulse echo method. Ultrasonic velocity, ultrasonic attenuation and rate of screen heights of successive peaks were determined according to the pulse-echo method by using 2 MHz and 4 MHz probes. It was observed that the mean grain size of samples has been changed with the sintering temperature. The velocity was found to be pretty sample dependent at room temperature and increased with increasing sintering temperature. The ultrasonic attenuation at room temperature was found to be more sample dependent. The sintering temperature variation of ultrasonic attenuation exhibited broad minimum values around 1200• C and sharp maximum values at 500• C. The increase observed in the temperature variation of longitudinal velocities and attenuation has been qualitatively explained with the help of the temperature variation of decrease value.

No abstract

No abstract

Sondaj çamuru kuyu tabanın temizlenmesi, yüksek basınçlı formasyonları kontrol etme, korozyona karşı koruma gibi önemli görevleri yerine getiren hayati derece öneme sahip bir akışkandır. Bu çalışmada Al 2 O 3 NP/ÇDKNT; kimyasal buhar biriktirme (CVD) yöntemi ile üretilmiş, X-Işını Fotoelektron Spektroskopisi (XPS) ve Geçirimli Elektron Mikroskobu (TEM) ile karakterize edilmiş, ardından su bazlı sondaj çamurlarına farklı oranlarda (0.001 -0.01% k/h) eklenmiştir. Hazırlanan sondaj çamurlarının plastik viskozitesi (PV), görünür viskozitesi (AV), kopma noktası (YP), jel mukavemeti (10 saniye ve 10 dakika) gibi reolojik analizleri FANN viskozimetresi ile, sıvı (filtrasyon) kaybı ve sondaj çamuru kek kalınlığı analizleri de Amerikan Petrol Enstitüsü (API) sıvı kaybı test ekipmanları ile API standartlarına uygun olacak şekilde yapılmıştır. Katkısız su bazlı sondaj çamuru ile karşılaştırıldığında; Al 2 O 3 NP/ÇDKNT'ün su bazlı sondaj çamurlarının PV değerini %85.7, AV değerini %41.8, YP değerini %20, 10 saniye ve 10 dakika değerlerini sırasıyla %16.6 ve %11 oranında arttırdığı, filtrasyon kaybı değerini %13.8 oranında azalttığı; aynı zamanda kek kalınlığı değerini de %18.5 oranında arttığı görülmüştür.

This novel research, aimed to improve the properties of Na-bentonite water based drilling mud (WBDM) and reduce its cost by adding multi-walled carbon nanotubes functionalized with copper oxide nanoparticles (CuONPs/MWCNTs). For this purpose, fistly, copper oxide nanoparticles (CuONPs) and multi-walled carbon nanotubes (MWCNTs) were synthesized separately, then MWCNTs were functionalized with CuONPs by chemical vapor deposition (CVD) method. Secondly, CuONPs/MWCNTs were characterized by X-ray Photoelectron Spectroscopy (XPS) and Scanning Electron Microscopy (SEM). Thirdly, CuONPs/ MWCNTs nanocomposite was added to the WBDM at different rates (0.001 to 0.01% w/v). Finally, rheological, filtration loss and cake thickness property analyzes were performed according to API standarts. As a result of this study, a significant improvement was observed in the rheological and filtration loss properties of WBDM with the addition of small amounts of CuONPs/MWCNTs. In particular, plastic viscosity (PV), apparent viscosity (AV), yield point (YP), 10 s and 10 min values increased by 57%, 36.7%, 28%, 33.3% and 44.4% respectively, the value of fitration loss decreased by 13.8%. With this improvement will increase the lifetime of the drilling mud is determined and its costs will decrease.

Bu çalışmada, su bazlı sondaj çamuruna (Na-Bentonit bazlı) fonksiyonelleştirilmiş karbon nanotüpün etkisinin tespiti amaçlanmıştır. Bu kapsamda su bazlı sondaj çamurları hazırlanmış ve kimyasal buhar biriktirme (CVD) yöntemi ile üretilen TiO2 nanopartikülü ile fonksiyonelleştirilmiş çok duvarlı karbon nanotüp (TiO2NP/ÇDKNT) farklı oranlarda (0.001 -0.01 % k/h) eklenmiştir. Hazırlanan sondaj çamurlarının plastik viskozitesi (PV), görünür viskozitesi (AV), kopma noktası (YP), jel mukavemeti değerleri (10 saniye ve 10 dakika) gibi reolojik özellikleri FANN viskozimetresi ile ayrıca su (filtrasyon) kaybı ve sondaj çamuru kek kalınlığı Amerikan Petrol Enstitüsü (API) sıvı kaybı test ekipmanları ile API standartlarına uygun olacak şekilde detaylı analiz edilmiştir. TiO2NP/ÇDKNT'ün eklenmesi ile hazırlanan sondaj çamurlarının reolojik ve filtrasyon özellikleri kendi içlerinde, daha sonra da katkısız sondaj çamuru ile karşılaştırılmıştır. Elde edilen sonuçlara göre; TiO2NP/ÇDKNT'ün su bazlı sondaj çamuruna eklenmesiyle; PV değerinin % 71.4; AV değerinin % 41.8; YP değerinin % 28; 10 saniye değerinin % 8.3; 10 dakika değerinin % 5.6 arttığı; filtrasyon kaybının % 8.6 azaldığı; aynı zamanda da kek kalınlığı değerinin de % 11 oranında arttığı görülmüştür. Yapılan bu çalışmayla; TiO2NP/ÇDKNT'ün sondaj çamurunun reolojik özellikleri ile filtrasyon kaybı değerlerine olumlu yönde katkı sağladığı tespit edilmiştir.Anahtar kelimeler: Su bazlı sondaj çamuru, nanopartikül madde, fonksiyonelleştirilmiş çok katmanlı karbon nanotüp, kimyasal buhar biriktirme yöntemi Effect of TiO2 Nanoparticle Functionalized Multi-Walled Carbon Nanotubes on the Water Based DrillingFluid: Experimental Study ABSTRACT: In this study, it is aimed to determine the effect of functionalized carbon nanotube on water-based drilling mud (Na-Bentonite based). In this context, water based drilling muds were prepared and multi-walled carbon nanotube (TiO2NP/MWCNTs) functionalized with TiO2 nanoparticle produced by chemical vapor deposition (CVD) method was added in different ratios (0.001 -0.01% w/v). The rheological properties of the prepared drilling muds such as plastic viscosity (PV), apparent viscosity (AV), yield point (YP), gel strength values (10 seconds and 10 minutes) were determined with a FANN viscometer, as well as water (filtration) loss and drilling mud cake thickness have been analyzed using American Petroleum Institute liquid loss test equipment accordance API standards in detail. The rheological and filtration properties of the drilling muds prepared by adding TiO2NP/MWCNTs were compared with each other and then with pure drilling mud. According to the results obtained; 71.4% of PV, 41.8% of AV value, 28% of the YP value, 8.3% of 10 seconds, 5.6% of 10 minutes increased and 8.6% of the loss of filtration decreased by adding TiO2NP/MWCNTs to water based drilling mud. At the same time, cake thickness value increased by 11%. With this study; it was found that TiO2NP/MWCNTs contributed positively to the rheological properties and filtration loss valu...