The polymerization of aminoethyl elaidamide in Langmuir and Langmuir−Blodgett films has been
studied. In Langmuir films, changes induced by the polymerization process were investigated by pressure/area isotherm measurements and after transfer of the irradiated film by scanning force microscopy and
IR spectroscopy. The pressure/area isotherms showed a phase transition at 16 mN/m, vanishing when the
irradiation time is increased. At low resolution, scanning force microscopy images revealed that the
irradiation induced the formation of structured domains. The shapes of these domains and the area occupied
by these domains are dependent on irradiation time. At intermediate resolution, these domains which
correspond to the polymeric phase appeared to be constituted of fibrillar structures characteristic of a
crystalline polymer. Besides these domains, the film has a similar structure to the monomer film. For the
polymerization in LB films, the changes in the structure of the film were followed by scanning force
microscopy and IR spectroscopy as a function of irradiation time. Few changes in surface topography were
observed at the micrometer scale during the polymerization. However we observed an increase of tip/sample interactions with irradiation time; moreover the irradiated film was found to be unsoluble. These
results are indirect proofs of the polymerization.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.