The gamma radiation had a significant detrimental effect on bond strength to human enamel and dentin when the adhesive restorative procedure was carried out after radiotherapy.
The effectiveness of mouthwash protocols in preventing gamma irradiation therapy damage to the ultimate tensile strength (UTS) of enamel and dentin is unknown. It was hypothesized that the use of chlorhexidine and fluoride mouthwash would maintain the UTS of dental structures. One hundred and twenty teeth were divided into 2 groups: irradiated (subjected to 60 Gy of gamma irradiation in daily increments of 2 Gy) and non-irradiated. They were then subdivided into 2 mouthwash protocols used 3 times per day: 0.12% chlorhexidine, 0.05% sodium fluoride, and control group (n = 10). The specimens were evaluated by microtensile testing. The results of the Tukey test (p < 0.05) indicated that the gamma irradiation therapy significantly reduced the UTS of the enamel, crown, and root dentin. Macromolecular alterations were suggested by optical retardation data in dentin. Structural alterations, in both substrates, were detected by scanning electron microscopy analysis. Mouthwash with 0.12% chlorhexidine partially prevented the damage to the mechanical properties of the irradiated crown dentin, whereas the 0.05% sodium-fluoride-irradiated enamel showed UTS similar to that of non-irradiated enamel.
The retention of glass fibre posts remained unaffected by surface roughness but was influenced by resin cement type. The self-adhesive cement RelyX Unicem yielded a significantly greater (P < 0.001) bond strength value when cementing the fibreglass posts.
Resin cements have led to great advances in dental ceramic restoration techniques because of their ability to bond to both dental structures and restorative materials. Objective The aim of this study was to assess the performance of resin cements when different curing modes are used, by evaluating the degree of conversion and bond strength to a ceramic substrate.Material and Methods Three resin cements were evaluated, two dual-cured (Variolink II and RelyX ARC) and one light-cured (Variolink Veneer). The dual-cured resin cements were tested by using the dual activation mode (base and catalyst) and light-activation mode (base paste only). For degree of conversion (DC) (n=5), a 1.0 mm thick feldspathic ceramic disc was placed over the resin cement specimens and the set was light activated with a QTH unit. After 24 h storage, the DC was measured with Fourier transform infrared spectroscopy (FTIR). For microshear bond strength testing, five feldspathic ceramic discs were submitted to surface treatment, and three cylindrical resin cement specimens were bonded to each ceramic surface according to the experimental groups. After 24 h, microshear bond testing was performed at 0.5 mm/min crosshead speed until the failure. Data were submitted to one-way ANOVA followed by Tukey test (p<0.05). Scanning electron microscopy (SEM) was used for classifying the failure modes.Results Higher DC and bond strength values were shown by the resin cements cured by using the dual activation mode. The Variolink II group presented higher DC and bond strength values when using light-activation only when compared with the Variolink Veneer group.Conclusion The base paste of dual-cured resin cements in light-activation mode can be used for bonding translucent ceramic restorations of up to or less than 1.0 mm thick.
RT causes changes that contribute to increased risk of tooth decay. Restorative treatments can be performed using adhesive procedures, but it is preferable to be performed before of the irradiation protocol, to guarantee better adhesive properties to restoration.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.