A new series of panchromatic ruthenium(II) sensitizers derived from carboxylated terpyridyl complexes of tris-thiocyanato Ru(II) have been developed. Black dye containing different degrees of protonation [(C(2)H(5))(3)NH][Ru(H(3)tcterpy)(NCS)(3)] 1, [(C(4)H(9))(4)N](2)[Ru(H(2)tcterpy)(NCS)(3)] 2, [(C(4)H(9))(4)N](3)[Ru(Htcterpy)(NCS)(3)] 3, and [(C(4)H(9))(4)N](4)[Ru(tcterpy)(NCS)(3)] 4 (tcterpy = 4,4',4' '-tricarboxy-2,2':6',2' '-terpyridine) have been synthesized and fully characterized by UV-vis, emission, IR, Raman, NMR, cyclic voltammetry, and X-ray diffraction studies. The crystal structure of complex 2 confirms the presence of a Ru(II)N6 central core derived from the terpyridine ligand and three N-bonded thiocyanates. Intermolecular H-bonding between carboxylates on neighboring terpyridines gives rise to 2-D H-bonded arrays. The absorption and emission maxima of the black dye show a bathochromic shift with decreasing pH and exhibit pH-dependent excited-state lifetimes. The red-shift of the emission maxima is due to better pi-acceptor properties of the acid form that lowers the energy of the CT excited state. The low-energy metal-to-ligand charge-transfer absorption band showed marked solvatochromism due to the presence of thiocyanate ligands. The Ru(II)/(III) oxidation potential of the black dye and the ligand-based reduction potential shifted cathodically with decreasing number of protons and showed more reversible character. The adsorption of complex 3 from methoxyacetonitrile solution onto transparent TiO(2) films was interpreted by a Langmuir isotherm yielding an adsorption equilibrium constant, K(ads), of (1.0 +/- 0.3) x 10(5) M(-1). The amount of dye adsorbed at monolayer saturation was (n(alpha) = 6.9 +/- 0.3) x 10(-)(8) mol/mg of TiO(2), which is around 30% less than that of the cis-di(thiocyanato)bis(2,2'-bipyridyl-4,4'-dicarboxylate)ruthenium(II) complex. The black dye, when anchored to nanocrystalline TiO(2) films achieves very efficient sensitization over the whole visible range extending into the near-IR region up to 920 nm, yielding over 80% incident photon-to-current efficiencies (IPCE). Solar cells containing the black dye were subjected to analysis by a photovoltaic calibration laboratory (NREL, U.S.A.) to determine their solar-to-electric conversion efficiency under standard AM 1.5 sunlight. A short circuit photocurrent density obtained was 20.5 mA/cm(2), and the open circuit voltage was 0.72 V corresponding to an overall conversion efficiency of 10.4%.

During the past five years, we have developed in our laboratory a new type of solar cell that is based on a photoelectrochemical process. The light absorption is performed by a monolayer of dye (i.e., a Ruthenium complex) that is adsorbed chemically at the surface of a semiconductor (i.e., titanium oxide (TiO2)). When excited by a photon, the dye has the ability to transfer an electron to the semiconductor. The electric field that is inside the material allows extraction of the electron, and the positive charge is transferred from the dye to a redox mediator that is present in solution. A respectable photovoltaic efficiency (i.e., 10%) is obtained by the use of mesoporous, nanostructured films of anatase particles. We will show how the TiO2 electrode microstructure influences the photovoltaic response of the cell. More specifically, we will focus on how processing parameters such as precursor chemistry, temperature for hydrothermal growth, binder addition, and sintering conditions influence the film porosity, pore‐size distribution, light scattering, and electron percolation and consequently affect the solar‐cell efficiency.

The ruthenium complexes [Ru(dcbpyH(2))(2)(Cl)(2)] (1), [Ru(dcbpyH(2))(2)(NCS)(2)] (2), (Bu(4)N)(4)[Ru(dcbpy)(2)(NCS)(2)] (3), and (Bu(4)N)(2)[Ru(dcbpyH)(2)(NCS)(2)] (4) were synthesized and characterized by cyclic voltammetry, UV-vis absorption, and emission, IR, Raman, and NMR spectroscopy. The absorption and emission maxima of these complexes red shifted with decreasing pH, and showed pH-dependent excited-state lifetimes. The ground-state pK(a) values were determined by spectrophotometeric methods, and the dissociation of protons was found to occur in two steps (pK(a) = 3 and 1.5). The Ru(II)/(III) couple in the complex (Bu(4)N)(4)[Ru(dcbpy)(2)(NCS)(2)] is shifted ca. 290 mV negatively with regard to that of the complex [Ru(dcbpyH(2))(2)(NCS)(2)] due to the replacement of H(+) by tetrabutylammonium cation. The negative shift for the dcbpy-based reduction potential is even larger, i.e., about 600 mV compared to that of the complex [Ru(dcbpyH(2))(2)(NCS)(2)]. The effect of deprotonation on the performance of these complexes as photosensitizers for nanocrystalline titania was investigated.

The adsorption of formate and acetate from aqueous solutions at pH 3-9 onto the TiO 2 rutile (110) surface was studied by ATR-FTIR spectroscopy. The spectra indicated that there was only one type of adsorbed species, and that formate and acetate were adsorbed in a similar manner. On the basis of the measured ν as -(COO)ν s (COO) splitting (∆ν as-s ) of 191 and 87 cm -1 , for formate and acetate, respectively, the monodentate (ester type) binding mode could be excluded. Ab initio calculations at the Hartree-Fock level showed that for pentacoordinated Ti IV , present in the (110) surface, the chelating bidentate binding mode is unstable with respect to the rearrangement to the monodentate or the bridging bidentate mode. The computed vibrational frequencies of formate and acetate adsorbed in a bridging bidentate mode onto Ti clusters with 2-5 Ti centers, representing the (110) surface, agreed with experiment and thus showed that this methodology can be used for the determination of the structures of adsorbates on, for example, metal oxide surfaces in contact with aqueous solutions.

Structural data have been obtained for the photosensitizer bis[(4,4‘-carboxy-2,2‘-bipyridine)(thiocyanato)]ruthenium(II) (1) via X-ray diffraction analysis. Crystals of 1 are triclinic, a = 11.4663(4) Å, b = 12.5897(5) Å, c = 18.9329(7) Å, α = 75.238(2)°, β = 89.611(2)°, γ = 66.446(2)°, space group P1̄, Z = 2, refinement to R = 0.0809, R w = 0.0950 for 4045 observed reflections. Structural models of sensitizer molecules anchoring to the TiO2 anatase surface and models of close-packed sensitizer monolayers with different anchoring types have been built by using experimental geometry of known organic Ti complexes and the X-ray structure of sensitizer 1. On the basis of a simple one-dimensional tight-binding model, it was suggested that possible modifications of TiO2/sensitizer interface could enhance interfacial transparency for injected electrons.

Nanocrystalline titanium dioxide colloids have been synthesized using a sol-gel technique followed by growth under hydrothermal conditions in a basic environment at temperatures between 190 and 270 °C. Thin films have been made from aqueous suspensions of these colloids. X-ray analysis showed the colloids to be primarily the anatase crystal phase. Scanning electron microscopy (SEM) revealed a predominantly rodlike particle morphology after growth at lower temperatures and the formation of principally truncated tetragonal or tetrahydral bipyramidal nanocrystallites following growth at higher temperatures. The rodlike particles self-organize into regular cubic arrays with the long axis of the rods aligned perpendicular to the film surface. This self-organization is dependent upon the base used in colloidal synthesis and also upon the dielectric constant of the medium used during film formation.

We report the results of an investigation on the preparation, spectral, and photoelectrochemical properties of Ru(II)-polypyridyl complexes containing a new phosphonated terpyridine (P-terpy) ligand: [Ru(H(2)P-terpy)(2)] and [Ru(HP-terpy)(Me(2)bpy)(NCS)]. Resonance Raman spectral and luminescence studies allow probing into the nature of the low-energy MLCT transitions observed in these complexes. The crystal and molecular structure of the mixed-ligand complex [Ru(HP-terpy)(Me(2)bpy)(NCS)] based on X-ray diffraction study is reported. This complex appears to be a promising candidate as a photosensitizer in dye-sensitized photoelectrochemical cells based on nanocrystalline films of TiO(2).

Scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), and X-ray powder diffraction (XRD) studies on nanocrystalline TiO2 powders and thin films are presented. The size, shape (mostly exposed faces), and ordering of the TiO2 anatase particles in the nanocrystalline films are discussed. The use of the topochemical approach, which considers the properties of (nanocrystalline) solids in terms of crystallographic features of (nano)crystals is suggested. The surface area of sensitizer [bis(4,4‘-dicarboxy-2,2‘-bipyridine)bis(thiocyanato)]ruthenium(II) [abbreviated as (cis-Ru(dcbpy)2(NCS)2] on the semiconductor surface for the different types of anchoring is estimated on the basis of single-crystal X-ray diffraction studies of the esterified form of the complex.