In the current study, an as-cast 26% Cr high chromium cast iron (HCCI) alloy was subjected to dry-sliding linear wear tests, under different loads. The loads were selected based on analytically computing the critical load (PC) i.e., the load necessary to induce plastic deformation. The PC was calculated to be 15 N and accordingly, a sub-critical load (5 N) and an over-critical load (20 N) were chosen. The influence of increasing the load during the wear test was investigated in terms of the matrix microstructural behaviour and its ability to support the surrounding carbides. The morphological aspects of the wear tracks, and the deformed matrix microstructure adjacent and underneath the track was analysed by confocal laser scanning microscope (CLSM) and scanning electron microscope (SEM), respectively. No evidence of plastic deformation of the matrix was observed below PC. On the contrary, at loads equal to and higher than PC, the austenitic matrix plastically deformed as evidenced by the presence of slip bands. Electron backscattered diffraction (EBSD) measurements in terms of grain reference orientation deviation, and micro-Vickers hardness of the austenitic matrix indicated a deformation depth of about 40 µm at the maximum applied load of 20 N. The active wear mechanisms during sliding were a combination of both adhesive and abrasive wear, although increasing the load shifted the dominant mechanism towards abrasion. This was primarily attributable to the increased propensity for carbide cracking and fracturing, combined with the inability of the hardened austenitic matrix surface and sub-surface to adequately support the broken carbide fragments. Moreover, the shift in the dominant wear mechanism was also reflected in the wear volume and subsequently, the wear rate.
In the current study, electrolytic deposition using two different electrodes, copper (Cu) and nickel (Ni) was investigated with the aim of protecting the worn surface during mechanical sectioning and polishing, for a posterior examination of the sub-surface microstructure. The efficacies of the two coatings were visually assessed based on its adhesivity and the ability to protect the wear tracks of an as-cast 26% Cr high chromium cast iron (HCCI) alloy. It was observed that electrodeposition using Cu as the electrode was ineffective owing to a poor adhesivity of the coating on the HCCI surface. The coating had peeled off at several regions across the cross-section during the mechanical sectioning. On the other hand, Ni electroplating using Ni strike as the electrolyte was successfully able to protect the wear track, and the sub-surface characteristics of the wear track could be clearly visualized. A uniform coating thickness of about 8 µm was deposited after 30–40 min with the current density maintained between 1 and 5 A/dm2. The presence of the Ni coating also acted as a protective barrier preventing the ejection of the broken carbide fragments underneath the wear track.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.