The Si(001) surface deoxidized by short annealing at T ~ 925°C in the ultrahigh vacuum molecuar beam epitaxy chamber has been in situ investigated using high-resolution scanning tunneling microscopy (STM)and redegreesected high-energy electron diffraction (RHEED. RHEED patterns corresponding to (2 × 1) and (4 × 4) structures were observed during sample treatment. The (4 × 4) reconstruction arose at T ≲ 600°C after annealing. The reconstruction was observed to be reversible: the (4 × 4) structure turned into the (2 × 1) one at T ≳ 600°C, the (4 × 4) structure appeared again at recurring cooling. The c(8 × 8) reconstruction was revealed by STM at room temperature on the same samples. A fraction of the surface area covered by the c(8 × 8) structure decreased, as the sample cooling rate was reduced. The (2 × 1) structure was observed on the surface free of the c(8 × 8) one. The c(8 × 8) structure has been evidenced to manifest itself as the (4 × 4) one in the RHEED patterns. A model of the c(8 × 8) structure formation has been built on the basis of the STM data. Origin of the high-order structure on the Si(001) surface and its connection with the epinucleation phenomenon are discussed.PACS 68.35.B-·68.37.Ef·68.49.Jk·68.47.Fg
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.