The influence of rapid thermal annealing effect on the electrical and structural properties of Au/Cu Schottky contacts on n-InP has been investigated by the current-voltage (I-V), capacitance-voltage (C-V), auger electron spectroscopy (AES) and the X-ray diffraction (XRD) techniques. As-deposited sample has a barrier height of 0.64 eV (I-V), 0.76 eV (C-V) which increases to 0.82 eV (I-V), 1.04 eV (C-V) after annealing at 400°C for 1min in nitrogen ambient. However, the barrier height decreases to 0.75 eV (I-V), 0.88 eV (C-V) after annealing at 600°C for 1min. Norde method is also employed to calculate the barrier heights of Au/Cu Schottky rectifiers and the values are 0.66 eV for as-deposited, 0.83 eV for 400°C and 0.76 eV for 600°C annealed contacts. These values are in good agreement with the values obtained from I-V method. From the above observations, it is clear that the Schottky barrier height increases with annealing temperatures up to 400°C. Thus, the optimum annealing temperature for the Au/Cu Schottky contact is 400 o C. Based on the AES and XRD results, the formation of indium phases at the Au/Cu/n-InP interface may be responsible for the increase in the barrier height for the contact annealed at 400°C and a corresponding decrease in leakage current. The decrease in the barrier height after annealing at 500 o C may be due to the formation of CuP and Au-P interfacial compounds at the interface. The AFM results showed that the surface morphology of Au/Cu Schottky contact is fairly smooth even after annealing at 500°C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.