The pulp and paper industry generates substantial amounts of solid waste and wastewater, which contain waste fibres. The potential of using these recycled wood fibres for producing eco-friendly composites that were bonded with a formaldehyde-free adhesive (magnesium lignosulfonate) and their use in structural applications was evaluated in this study. Fibreboards were produced in the laboratory with a density of 720 kg·m−3 and 15% magnesium lignosulfonate gluing content, based on the dry fibres. The mechanical properties (bending strength, modulus of elasticity and internal bond strength), physical properties (thickness swelling and water absorption) and formaldehyde content were determined and compared with the European Standards requirements for wood-based panels. In general, the laboratory-produced panels demonstrated acceptable mechanical properties, such as bending strength (18.5 N·mm−2) and modulus of elasticity (2225 N·mm−2), which were higher than the minimum requirements for type P2 particleboards and equal to the requirements for MDF panels. The moisture properties, i.e., thickness swelling (24 h) and water absorption (24 h) significantly deteriorated. The free formaldehyde content of the laboratory-produced composites (1.1 mg/100 g) reached the super E0 grade (≤1.5 mg/100 g), which allowed for their classification as eco-friendly, low-emission wood-based composites. The L-type corner joints, made from the developed composites, demonstrated significantly lower bending capacity (from 2.5 to 6.5 times) compared to the same joints made from MDF panels. Nevertheless, the new eco-friendly composites can be efficiently utilised as a structural material in non-load-bearing applications.

In recent years, the furniture design trends include ensuring ergonomic standards, development of new environmentally friendly materials, optimised use of natural resources, and sustainably increased conversion of waste into value-added products. The circular economy principles require the reuse, recycling or upcycling of materials. The potential of reusing waste corrugated cardboard to produce new lightweight boards suitable for furniture and interior applications was investigated in this work. Two types of multi-layered panels were manufactured in the laboratory from corrugated cardboard and beech veneer, bonded with urea-formaldehyde (UF) resin. Seven types of end corner joints of the created lightweight furniture panels and three conventional honeycomb panels were tested. Bending moments and stiffness coefficients in the compression test were evaluated. The bending strength values of the joints made of waste cardboard and beech veneer exhibited the required strength for application in furniture constructions or as interior elements. The joints made of multi-layer panels with a thickness of 51 mm, joined by dowels, demonstrated the highest bending strength and stiffness values (33.22 N∙m). The joints made of 21 mm thick multi-layer panels and connected with Confirmat had satisfactory bending strength values (10.53 N∙m) and Minifix had the lowest strength values (6.15 N∙m). The highest stiffness values (327 N∙m/rad) were determined for the 50 mm thick cardboard honeycomb panels connected by plastic corner connector and special screw Varianta, and the lowest values for the joints made of 21 mm thick multi-layer panels connected by Confirmat (40 N∙m/rad) and Minifix (43 N∙m/rad), respectively. The application of waste corrugated cardboard as a structural material for furniture and interiors can be improved by further investigations.