Hot rolled, laboratory-cast, TWIP steel samples (5.4 mm thick) of 22% Mn - 0.6% C (in mass-%) were cold rolled to different reductions (from 40 % to 70 %) and subsequently isothermally annealed for various times at temperatures ranging from 450º C to 1100º C. The evolution of recrystallization and grain growth was followed by control of the softening kinetics complemented by metallographic, OIM and microtexture observations. A map of the recovery, recrystallization and grain growth in the temperature-time space was obtained. In all instances, the grain size at the end of recrystallization was very fine, D ≤ 2 µm and larger grain sizes were the result of grain growth. A range of grain sizes 2 µm ≤ D ≤ 50 µm was covered by the grain growth experiments. A phenomenological grain growth equation that is useful for the annealing control of this steel was derived from the measurements.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.