A new series of thin film composite membranes with high CO2 permeance (up to 8000 GPU) and CO2/N2 selectivity (up to 55.7) was designed and fabricated via coating PIM-1 solution in a mixture of chloroform and trichloroethylene on top of a cross-linked PTMSP gutter layer.
The mitigation of the physical aging of thin-film composite (TFC) poly[1-trimethylsilyl-1-propyne] (PTMSP) membranes was studied via the simultaneous application of a polymer-selective layer crosslinking and mixed-matrix membrane approach. For the first time, a recently developed highly porous activated carbon material (infrared (IR) pyrolyzed poly[acrylonitrile] (PAN) or IR-PAN-a) was investigated as an additive to a PTMSP-selective layer for the reduction of aging in TFC membranes. The total electric energy spent on the IR irradiation treatment of IR-PAN-a particles was twice lower than conventional heating. The flat-sheet porous microfiltration membrane MFFK-1 was used as a support, and the crosslinked PTMSP/PEI loaded with a porous filler was applied as a selective layer (0.8–1.8 µm thick) to the TFC membranes. The initial IR-PAN-a sample was additionally milled to obtain a milled IR-PAN-aM sample with a monomodal particle size distribution of 500–800 nm. It was shown that IR-PAN-a, as a filler material with a high surface area and pore volume (2450 m2/g and 1.06 cm3/g, respectively) and a well-developed sponge-like structure, leads to the increase of the N2, O2, and CO2 permeance of PTMSP-based hybrid membrane material and the decrease of the aging of PTMSP. The simultaneous effect of crosslinking and the addition of a highly porous filler essentially improved the aging behavior of PTMSP-based TFC membranes. The monomodal and narrow particle size distribution of highly porous activated IR-pyrolyzed PAN is a key factor for the production of TFC membranes with reduced aging. The highest stability was achieved by the addition of a milled IR-PAN-aM sample (10 wt%). TFC membrane permeance was 6300 GPU (30% of initial permeance) after 11,000 h of aging at ambient laboratory conditions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.