No abstract

The development of new glassy materials is key for addressing major global challenges in energy, medicine, and advanced communications systems. For example, thin, flexible, and large-area glass substrates will play an enabling role in the development of flexible displays, roll-to-roll processing of solar cells, next-generation touch-screen devices, and encapsulation of organic semiconductors. The main drawback of glass and its limitation for these applications is its brittle fracture behavior, especially in the presence of surface flaws, which can significantly reduce the practical strength of a glass product. Hence, the design of new ultrastrong glassy materials and strengthening techniques is of crucial importance. The main issues regarding glass strength are discussed, with an emphasis on the underlying microscopic mechanisms that are responsible for mechanical properties. The relationship among elastic properties and fracture behavior is also addressed, focusing on both oxide and metallic glasses. From a theoretical perspective, atomistic modeling of mechanical properties of glassy materials is considered. The topological origin of these properties is also discussed, including its relation to structural and chemical heterogeneities. Finally, comments are given on several toughening strategies for increasing the damage resistance of glass products.

The increase of retinal vessel oxygen saturation in diabetic retinopathy points to a diabetic microvascular alteration. This may be due to occlusions and obliterations in the capillary bead and the formation of arterio-venous shunt vessels. On the other hand, hyperglycaemia-induced endothelial dysfunction, with subsequent suppression of the endothelial NO-synthase and disturbance of the vascular auto-regulation, may contribute to retinal tissue hypoxia.

Bulk metallic glasses (BMGs) generally fail in a brittle manner under uniaxial, quasistatic loading at room temperature. The lack of plastic strain is a consequence of shear softening, a phenomenon that originates from shear-induced dilation that causes plastic strain to be highly localized in shear bands. So far, significant tensile ductility has been reported only for microscopic samples of around 100 nm (ref. 4) as well as for high strain rates, and so far no mechanisms are known, which could lead to work hardening and ductility in quasistatic tension in macroscopic BMG samples. In the present work we developed CuZr-based BMGs, which polymorphically precipitate nanocrystals during tensile deformation and subsequently these nanocrystals undergo twinning. The formation of such structural heterogeneities hampers shear band generation and results in macroscopically detectable plastic strain and work hardening. The precipitation of nanocrystals and their subsequent twinning can be understood in terms of a deformation-induced softening of the instantaneous shear modulus. This unique deformation mechanism is believed to be not just limited to CuZr-based BMGs but also to promote ductility in other BMGs.

No abstract

We report on phase formation of a multicomponent Zr66.4Nb6.4Cu10.5Ni8.7Al8 glass-forming alloy upon copper mold casting. A bcc phase embedded in a glassy matrix forms for moldcast bulk samples yielding an in-situ bulk metallic glass matrix composite upon slow cooling from the melt. Upon annealing, the first exothermic transformation of the material is related to precipitation of an icosahedral phase from the glassy matrix. The formation of the bcc phase-containing metallic glass composite is strongly governed by the alloy composition and the actual cooling rate during solidification. Room-temperature compression tests reveal significant yielding and plastic deformation before failure.

No abstract

No abstract