An important aetiologic factor in the pathogenesis of denture-induced stomatitis, is the presence of numerous yeasts, usually Candida albicans, on the fitting surfaces of dentures. In the present study, effect of glow-discharge plasma, a technique applied to increase surface wettability of acrylic resins, on candidial adherence was evaluated. The durability of glow-discharge modification with saliva coating was also evaluated. Samples including control and experimental groups were prepared by using heat compression mould technique. To create a hydrophobicity gradient, experimental groups were exposed to a radiofrequency glow discharge in an O2 atmosphere under different discharge powers. To characterize the wetting properties, an expression of surface hydrophobicity, contact angle measurements were performed by the sessile drop method. The organism used was C. albicans (ATTC10321). Acrylic samples were coated with unstimulated whole saliva collected from a healthy man. The fungal suspension was poured on saliva-inoculated samples and incubated at 37 degrees for 2 h. The samples were then fixed with glutaraldehyde and Gram stained. Adhered candidial cells were examined by light microscope. Diffuse Reflectance FTIR (DRIFT) and scanning electron-microscope examinations were also performed to evaluate the surface composition and roughness of the test groups. Glow-discharge plasma was found to be an effective means of increasing surface wettability even with salivary pellicle. Amounts of candida cells adhered were significantly higher in all the plasma treated surfaces than the unmodified control group (P < 0.001). It was concluded that improving the surface wettability of acrylic resins by glow-discharge plasma in O2 atmosphere increased the adherence of the C. albicans.
The influence of porcelain thickness and opacity on the polymerization of two dual activated (microfine and hybrid) and one light irradiated (hybrid) resin cements was assessed by hardness measurements. The surface microhardness values of the upper and lower surface of 1 mm thick resin cement specimens were determined. Specimens were polymerized using 40s irradiation beneath different thicknesses and opacities of porcelain discs. The results showed that increasing the thicknesses and opacity of the porcelain produced a statistically significant decrease in microhardness of the resin-based cements. The effect of attenuation is less for the microfine cement than for the hybrids. In the case of hybrid cements, the light activated material performed better than the dual activated cement.
Introduction: Constuction of the obturator prostheses and providing the patient's comfort with them are very difficult. Primary and the most important stage for these prostheses is to perform a proper impression.
The aim of this study was to evaluate the level of residual monomer in acrylic denture base materials having different polymerization properties. The investigation included a conventional-type acrylic cured under heat and pressure, as well as a pour-type resin polymerized by an injection-moulding technique at room temperature and under pressure. It was found that the residual monomer content ranged from 0.22-0-54% in pour-type resin, and from 0.23-0-52% in routinely used resins when the specimens were analysed by high performance liquid chromatography. These findings revealed that there were no significant differences between the two types of acrylic in terms of their residual monomer content.
It has been suggested that altering the surface properties of acrylic resin material may change the nature of the adsorbed pellicle affecting denture retention and microbial adherence. This study aimed at evaluating the adsorption of salivary high molecular-weight mucins, a major component of denture pellicle, onto modified acrylic resin surfaces. (Poly) methylmethacrylate specimens were treated by glow discharge plasma technique, using hydrophilic 2-Hydroxyethylmethacrylate monomer or oxygen (O(2)) gas and hydrophobic Hexamethyldisiloxane monomer, at different discharge powers. Acrylic samples were incubated with high-molecular weight mucin, MG1 purified from saliva, the adsorbed fractions were transferred to nitrocellulose membranes by slot-blot technique, stained by periodic acid-Schiff and colour intensities were analysed by a colour densitometer. Higher amounts of mucins were adsorbed on all the surfaces modified by glow-discharge plasma treatment. Within the limitations of this study, it was concluded that glow-discharge plasma altered the surfaces of acrylic resin denture base materials and significantly increased the adsorption of high molecular-weight mucins at varying levels depending on plasma parameters.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.