The detailed characterization of solution‐derived nickel (II) oxide (NiO) hole‐transporting layer (HTL) films and their application in high efficiency organic photovoltaic (OPV) cells is reported. The NiO precursor solution is examined in situ to determine the chemical species present. Coordination complexes of monoethanolamine (MEA) with Ni in ethanol thermally decompose to form non‐stoichiometric NiO. Specifically, the [Ni(MEA)2(OAc)]+ ion is found to be the most prevalent species in the precursor solution. The defect‐induced Ni3+ ion, which is present in non‐stoichiometric NiO and signifies the p‐type conduction of NiO, as well as the dipolar nickel oxyhydroxide (NiOOH) species are confirmed using X‐ray photoelectron spectroscopy. Bulk heterojunction (BHJ) solar cells with a polymer/fullerene photoactive layer blend composed of poly‐dithienogermole‐thienopyrrolodione (pDTG‐TPD) and [6,6]‐phenyl‐C71‐butyric acid methyl ester (PC71BM) are fabricated using these solution‐processed NiO films. The resulting devices show an average power conversion efficiency (PCE) of 7.8%, which is a 15% improvement over devices utilizing a poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) HTL. The enhancement is due to the optical resonance in the solar cell and the hydrophobicity of NiO, which promotes a more homogeneous donor/acceptor morphology in the active layer at the NiO/BHJ interface. Finally, devices incorporating NiO as a HTL are more stable in air than devices using PEDOT:PSS.
Interface recombination induced by the defect states in zinc‐oxide‐nanoparticle‐based electron extraction layer is reported as a significant loss‐mechanism of photocurrent collection. By choosing appropriate UV–ozone treatment conditions on the zinc oxide layer, inverted polymer solar cells show reduced interface recombination and thus improved power conversion efficiencies of up to 8.1%.
Infrared, visible, and multispectral photodetectors are important components for sensing, security and electronics applications. Current fabrication of these devices is based on inorganic materials grown by epitaxial techniques which are not compatible with low‐cost large‐scale processing. Here, air‐stable multispectral solution‐processed inorganic double heterostructure photodetectors, using PbS quantum dots (QDs) as the photoactive layer, colloidal ZnO nanoparticles as the electron transport/hole blocking layer (ETL/HBL), and solution‐derived NiO as the hole transport/electron blocking layer (HTL/EBL) are reported. The resulting device has low dark current density of 20 nA cm‐2 with a noise equivalent power (NEP) on the order of tens of picowatts across the detection spectra and a specific detectivity (D*) value of 1.2 × 1012 cm Hz1/2 W‐1. These parameters are comparable to commercially available Si, Ge, and InGaAs photodetectors. The devices have a linear dynamic range (LDR) over 65 dB and a bandwidth over 35 kHz, which are sufficient for imaging applications. Finally, these solution‐processed inorganic devices have a long storage lifetime in air, even without encapsulation.
The VOC loss in several polymer-fullerene solar cells is determined. Based on these data, a major source of photovoltage loss is attributed to the low dielectric constants of the polymers. Such loss is close to zero if the dielectric constant of the polymer-fullerene blend is close to 5.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.