The aim of the present study was to determine the surface roughness of heat-treated Scots pine (Pinus sylvestris L.), Eastern beech (Fagus orientalis L.), Uludağ fir (Abies bornmülleriana Mattf.), and sessile oak (Quercus petraea L.) wood material samples following planing by the cutters of a horizontal milling machine. The samples that were heattreated at 140 ºC or 160 ºC for 3, 5, or 7 hours were then processed by star blades or razor blades, which are the most frequently used blade types in a milling machine. The surface roughness of the samples was determined by a touch (spined) scan device (TIME TR200), as indicated by the ISO 4287 principle. The results of the study indicate that heat treatment decreases the surface roughness value of the wood material and a significant difference in surface roughness cannot be detected between planing using the razor blade or the star blade.
Heat treatment is known to improve the stability and durability of various woods. However, in the process some surface properties are changed. This paper reports the changes in surface properties such as color, glossiness, pendulum hardness, and surface adhesion on coated heattreated and untreated beech wood. The wood was coated with an epoxy acrylic resin sealer followed by a polyacrylic-based resin varnish that is normally applied on parquet with single and double layers according to the manufacturer's recommendations. The results showed that in relation to color parameters, the lightness decreased while a* increased in response to heat treatment. This was followed by a decrease in the redness (a*) and a decrease in yellow (b*) with the intensity of the treatment. There was an initial increase in the glossiness but it decreased later on with the severity of the treatment. The hardness and adhesion also decreased with the severity of the treatment for beech coated with single and double layers. The wood surface properties depended on the treating time and the temperature of the treatment.
In the last few years there has been an increased demand to change the natural color of valuable hardwoods without chemicals for use mainly in indoor parquet floors. In this study, wood samples from oak (Quercus petraea L.), one of the most used species for parquet, were heat treated (ThermoWood method) at 190 °C for 2 h and at 212 °C for 1 and 2 h. Untreated and heat treated wood surfaces were coated following two different applications: type 1, with a single layer of sealer (50 g/m2) and type 2 with two layers (35 g/m2) using a nanolacke varnishing system. The objective of this study was to investigate surface properties including adhesion, glossiness, pendulum hardness, and color (L*, a*, b*, ΔE*, ΔL*, Δa*, and Δb*). With heat treatment the lightness decreases, and its decrease is higher for higher temperatures and treatment times. Type 2 coated wood presented a slightly lower lightness decrease. The experiment showed a slight increase followed by a decrease in redness (lower a*) and a clear decrease in the yellow tone (b*). The total color variation increased with the intensity of the treatment, while the glossiness decreased (more for Type 1 coated wood). The adhesion strength and surface hardness decreased with the heat treatment in both the Type 1 and Type 2 coated wood samples. The decrease in adhesion was higher for Type 2, reaching 67%, while the decrease in surface hardness reached about 18%.
Bu çalışmada, 212°C'de 1 saat ve 2 saat süreyle ısıl işlem (ThermoWood metot, Novawood Fabrikası, Gerede-Bolu, Türkiye) görmüş dişbudak (Fraxinus excelsior), kayın (Fagus orientalis L.), akçaağaç (Acer trautvetteri Medw.) ve kızılçam (Pinus resinosa) odunu türlerinin renk ve parlaklık değerleri incelenmiştir. Isıl işlemden sonra, bu ısıl işlem görmüş ağaç türlerinin renk ve parlaklık değerleri ısıl işlem görmemiş örnekler ile kıyaslanmıştır. Test sonuçlarına göre; ΔE* değerleri artmıştır. Isıl işlem süresinin artması ile dişbudak, kayın ve akçaağaç odunlarında L* ve b* parametreleri azalmıştır. a* parametresi kızılçam ve akçaağaç odunlarında ısıl işlem süresinin artması ile artmıştır. Isıl işlem süresinin artması ile 85°'de paralel ve dik parlaklık değerleri kızılçam ve akçaağaç odunlarında artmıştır. Isıl işlem sıcaklık ve süreleri odun örneklerinde renk ve parlaklık değerlerini değiştirmiştir.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.