The effect of V2O5addition on the microstructures and the microwave dielectric properties of 0.9CaWO4-0.1Mg2SiO4(9CWMS) ceramics prepared by conventional solid-state routes have been investigated. The V2O5were selected as liquid phase sintering aids to lower the sintering temperature of 9CWMS ceramics. A small amount of V2O5(0.25~1 wt%) were used for sintering aid and led to high densification at 1050°C. The dielectric properties of 9CWMS ceramics with V2O5additions are strongly dependent on the densification, the microstructure. As the amount of V2O5additives increased from 0.25 to 1.0 wt%, the dielectric constantsεrdecreased following the trend with density. The quality valuesQdecreased with the increase of V2O5amount for all sintering temperatures. The 0.25 wt% V2O5-doped 0.9CaWO4-0.1Mg2SiO4ceramicssintered at 1080°C for 2 h had the optimum dielectric properties: εr= 5.7;Q×f= 73000 (at 14 GHz).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.