Recoil pressure is a critical factor affecting the melt pool dynamics during Laser Powder Bed Fusion (LPBF) processes. Recoil pressure depresses the melt pool. When the recoil pressure is low, thermal conduction and capillary forces may be inadequate to provide proper fusion between layers. However, excessive recoil pressure can produce a keyhole inside the melt pool, which is associated with gas porosity. Direct recoil pressure measurements are challenging because it is localized over an area proportionate to the laser spot size producing a force in the mN range. This paper reports a vibration-based approach to quantify the recoil force exerted on a part in a commercial LPBF machine. The measured recoil force is consistent with estimates from high speed synchrotron imaging of entrained particles, and the results show that the recoil force scales with applied laser power and is inversely related to the laser scan speed. These results facilitate further studies of melt pool dynamics and have the potential to aid process development for new materials.
Copper powder in three different powder types were spheroidized using radio-frequency inductively coupled plasma (ICP) spheroidization process (TekSphero-15 system). The characterized powders include virgin powder as purchased from the powder manufacturer, powder used in electron beam powder bed fusion (EB-PBF) process, and reconditioned powder, which was used powder that underwent an oxygen-reduction treatment. The goal of spheroidizing these powder types was to evaluate the change in powder morphology, the possibility of enhancing the powder properties back to their as-received conditions, and assess oxygen reduction of the powder lots given their initial oxygen contents. Also, to investigate the impact of re-spheroidization on powder properties, the second round of spheroidization was performed on the already used-spheroidized powder. The impact of powder type on powder sphericity and particle size distribution was evaluated using the image analysis of scanning electron microscope (SEM) micrographs and laser diffraction, respectively. The spheroidized powder showed higher sphericity and more uniform particle size distribution overall. Depending on the powder collection bin, second round of spheroidization affected the powder sphericity differently. The possibility of deploying the plasma spheroidization process as an alternative oxygen-reduction technique was also investigated through tracking the powders’ oxygen content using inert gas fusion method before and after the spheroidization. The plasma spheroidized powder showed less oxygen content than the hydrogen-treated powder. The second round of spheroidization caused no change in oxygen content. The correlation between oxygen-reduction and created cracks was discussed and compared between plasma spheroidization and hydrogen-treatment. The plasma spheroidization process created a powder with higher sphericity, uniform particle size, and less oxygen content.
Recoil pressure is a critical factor affecting the melt pool dynamics during Laser Powder Bed Fusion (LPBF) processes. Recoil pressure depresses the melt pool, providing layer-to-layer fusion without introducing porosity. If the recoil pressure is too low, the process operates in a conduction mode where layers will not properly fuse, while excessive recoil pressure leads to a keyhole mode, which results in gas porosity. Direct recoil pressure measurements are challenging because it is localized over an area proportionate to the laser spot size producing a force in the mN range. This paper reports a vibration-based approach to quantify the recoil force exerted on a part in a commercial LPBF machine. The measured recoil force is consistent with estimates from high speed synchrotron imaging of entrained particles, and the results show that the recoil force scales with applied laser power and is inversely related to the laser scan speed. These results facilitate further studies of melt pool dynamics and have the potential to aid process development for new materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.