For various lighting and monolithic sensor systems application, vertically aligned three-dimensional (3D) gallium nitride (GaN)-and indium gallium nitride (InGaN)/ GaN-based LED nanowire arrays with sub-200 nm feature sizes (down to 35 nm) were fabricated using a nanosphere liftoff lithography (NSLL) technique combined with hybrid topdown etching (i.e., inductively coupled plasma dry reactive ion etching (ICP-DRIE) and wet chemical etching). Owing to the lithographic opening and well-controlled surface functionalization prior to the polystyrene nanosphere (PN) deposition, vertical GaN nanowire arrays with an area density of 9.74 × 10 8 cm −2 and an aspect ratio of >10 could be realized in a specified large area of 1.5 × 1.5 mm 2 . Optoelectrical characteristics of the nanoLEDs were further investigated in cathodoluminescence (CL) measurements, in which multiquantum well (MQW) shows a clear CL-emission at a wavelength of 465 nm. Thus, using NSLL to manufacture low-cost but highly ordered 3D GaN-based nanowires and nanoLEDs is a feasible alternative to other sophisticated but more expensive nanolithography methods.
In this work, we present conductometric gas sensors based on p-type calcium iron oxide (CaFe2O4) nanoparticles. CaFe2O4 is a metal oxide (MOx) with a bandgap around 1.9 eV making it a suitable candidate for visible light-activated gas sensors. Our gas sensors were tested under a reducing gas (i.e., ethanol) by illuminating them with different light-emitting diode (LED) wavelengths (i.e., 465–640 nm). Regardless of their inferior response compared to the thermally activated counterparts, the developed sensors have shown their ability to detect ethanol down to 100 ppm in a reversible way and solely with the energy provided by an LED. The highest response was reached using a blue LED (465 nm) activation. Despite some responses found even in dark conditions, it was demonstrated that upon illumination the recovery after the ethanol exposure was improved, showing that the energy provided by the LEDs is sufficient to activate the desorption process between the ethanol and the CaFe2O4 surface.
Vertically aligned 3D gallium nitride (GaN) nanowire arrays with sub-50 nm feature sizes were fabricated using a nanosphere lift-off lithography (NSLL) technique combined with hybrid top-down etching steps (i.e., inductively coupled plasma dry reactive ion etching (ICP-DRIE) and wet chemical etching). Owing to the well-controlled chemical surface treatment prior to the nanobead deposition and etching process, vertical GaN nanowire arrays with diameter of ~35 nm, pitch of ~350 nm, and aspect ratio of >10 could be realized using 500 nm polystyrene nanobead (PN) masks. This work has demonstrated a feasibility of using NSLL as an alternative for other sophisticated but expensive nanolithography methods to manufacture low-cost but highly ordered 3D GaN nanostructures.
Silicon and germanium pillar structures (i.e., micro-and nanowires) were fabricated by a top-down approach including nanoimprint lithography and cryogenic dry etching. Various etching parameters were tested to ensure a reliable fabrication process. The impression of nanomechanical properties of such 3-D structures were extracted experimentally by nanoindentation showing promising and comparative results to utilize such nanostructures as small force artefacts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.