Heteroatom-doped conductive carbon nanomaterials are promising for energy and catalysis applications, but there are few reports on increasing their heteroatom doping content and conductivity simultaneously. In this manuscript, we use 2-(4-aminophenyl)-5-aminobenzimidazole as the diamine monomer to prepare polyamic acid with asymmetric structural units doped with phosphoric acid (PA) and polyacrylonitrile (PAN) as innovative composite precursors, which are then electrospun into nanofiber films. After stabilization and carbonization, the electrospun fibers are converted into N/P co-doped electrospun carbon nanofiber films (ECNFs) with high heteroatom content, including 4.33% N and 0.98% P. The morphology, structure, and conductivity of ECNFs were systematically characterized. The ECNFs doped with 15 wt.% PA exhibited conductivity that was 47.3% higher than that of the ECNFs undoped with PA, but the BET surface area decreased by 23%. The doped PA in the precursor nanofibers participated in the cyclization of PAN during thermal stabilization, as indicated by infrared spectroscopy and thermogravimetric analysis results. X-ray diffraction and Raman results indicate that a moderate amount of PA doping facilitated the formation of ordered graphitic crystallite structures during carbonization and improved the conductivity of ECNFs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.