The effect of quaternary addition of Nb being from 0 to 2 mol% on the phase constitution, phase transformation behavior and shape memory behavior of Au-50 mol%Ti-15 mol%Co (AuTiCo) alloys is studied. X-ray diffraction analysis shows that, with increasing Nb concentration, the primary phase appeared at room temperature changes from B19 orthorhombic martensite phase to B2 cubic parent phase, and that all the lattice parameters are not largely changed by Nb addition. The maximum transformation strain evaluated in 2 mol%Nb-added AuTiCo is 7.4%. Differential scanning calorimetry revealed that the reverse martensitic transformation finish temperature (A f ) decreases from 414 K in Nb-free AuTiCo to 303 K by 2 mol%Nb addition. The ratio of A f change by Nb addition is evaluated to be ¹55 K/mol%Nb, that is comparably larger than ¹31 K/mol%Nb in NiTi. These results indicate that Nb addition is effective to stabilize B2 parent phase. AuTiCo alloy containing less than 2 mol%Nb exhibits shape memory effect with 90% shape recovery ratio. Besides, AuTiCo containing 2 mol%Nb exhibits 2.8% superelastic shape recovery at room temperature as well as 7.4% maximum transformation strain. Therefore, Nb addition to AuTiCo is effective to decrease the martensitic transformation temperature and to improve superelasticity, although the transformation temperature hysteresis increases by Nb addition, similar to Nb-added NiTi.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.