Lithium-sulfur batteries hold great promise for serving as next generation high energy density batteries. However, the shuttle of polysulfide induces rapid capacity degradation and poor cycling stability of lithium-sulfur cells. Herein, we proposed a unique lithium-sulfur battery configuration with an ultrathin graphene oxide (GO) membrane for high stability. The oxygen electronegative atoms modified GO into a polar plane, and the carboxyl groups acted as ion-hopping sites of positively charged species (Li(+)) and rejected the transportation of negatively charged species (Sn(2-)) due to the electrostatic interactions. Such electrostatic repulsion and physical inhibition largely decreased the transference of polysulfides across the GO membrane in the lithium-sulfur system. Consequently, the GO membrane with highly tunable functionalization properties, high mechanical strength, low electric conductivity, and facile fabrication procedure is an effective permselective separator system in lithium-sulfur batteries. By the incorporation of a permselective GO membrane, the cyclic capacity decay rate is also reduced from 0.49 to 0.23%/cycle. As the GO membrane blocks the diffusion of polysulfides through the membrane, it is also with advantages of anti-self-discharge properties.

The reversible electrochemical transformation from lithium (Li) and sulfur (S) into Li2 S through multielectron reactions can be utilized in secondary Li-S batteries with very high energy density. However, both the low Coulombic efficiency and severe capacity degradation limits the full utilization of active sulfur, which hinders the practical applications of Li-S battery system. The present study reports a ternary-layered separator with a macroporous polypropylene (PP) matrix layer, graphene oxide (GO) barrier layer, and Nafion retarding layer as the separator for Li-S batteries with high Coulombic efficiency and superior cyclic stability. In the ternary-layered separator, ultrathin layer of GO (0.0032 mg cm(-2) , estimated to be around 40 layers) blocks the macropores of PP matrix, and a dense ion selective Nafion layer with a very low loading amount of 0.05 mg cm(-2) is attached as a retarding layer to suppress the crossover of sulfur-containing species. The ternary-layered separators are effective in improving the initial capacity and the Coulombic efficiency of Li-S cells from 969 to 1057 mAh g(-1) , and from 80% to over 95% with an LiNO3 -free electrolyte, respectively. The capacity degradation is reduced from 0.34% to 0.18% per cycle within 200 cycles when the PP separator is replaced by the ternary-layered separators. This work provides the rational design strategy for multifunctional separators at cell scale to effective utilizing of active sulfur and retarding of polysulfides, which offers the possibility of high energy density Li-S cells with long cycling life.

Operando and kinetic studies of lean-burn methane combustion were preformed on a Pd­(3.3 wt %)/γ-Al2O3 catalyst in a low temperature range of 473–673 K. The reaction order with respect to oxygen decreased with temperature, and the order with respect to methane remained constant. The working catalyst is characterized using operando Raman spectroscopy and in situ diffuse reflectance infrared Fourier transform spectroscopy of CO adsorption (DRIFTS), and the Pd chemical states were measured with X-ray photoelectron spectroscopy (XPS). Partial oxidation of Pd atoms during reaction was identified by Raman and XPS spectroscopies. In particular, the DRIFT spectra revealed that ∼45% of Pd atoms at the top layers were transferred into PdO x species above 523 K. The reaction was assumed to occur primarily on the metallic Pd sites below 673 K, proceeding through the Langmuir–Hinshelwood mechanism, and Pd oxide may affect the adsorption and activation of reactants.