Li 4 SiO 4 was obtained by using quartz powder of different particle sizes (75−180 μm, 45−75 μm, 38−45 μm, and <38 μm) and Li 2 CO 3 as raw materials through a solid-state reaction at 720 °C. X-ray diffraction (XRD), scanning electron microscopy (SEM), and differential thermal analysis and thermogravimetry (DTA/TG) were used to examine the sintering behavior and properties of the samples. The results indicated that when the particle size of the quartz powder decreased, the solid-state reaction performed more completely, the content of the Li 4 SiO 4 phase increased, and the size of the grain agglomerates decreased gradually. The enhanced chemical reactivity of the quartz powder with Li 2 CO 3 and the shortened diffusion distance as the quartz size decreases are helpful to the formation of the Li 4 SiO 4 phase. The sorption analysis revealed that the samples synthesized using the quartz powder with smaller particle sizes experienced a more rapid absorption−desorption process with a higher absorption efficiency.
A zinc oxide (ZnO) nanoarray (rod‐like nanostructure) was successfully synthesized through a low‐temperature aqueous solution and microwave‐assisted synthesis using zinc nitrate hexahydrate (Zn(NO3)2·6H2O) and hexamethylenetetramine (HMTA) as raw materials, and using FTO glass as substrate. The effects of parameters in the preparation process, such as solution concentration, reaction temperature and microwave power, on the morphology and microstructure of ZnO nanoarray were studied. Phase structure and morphology of the products were characterized by X‐ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The results indicated that hexagonal wurtzite structure ZnO nanoarray with good crystallization could be prepared through a low‐temperature solution method. When the concentration of the mixed solution was 0.05 M, the reaction temperature was 95 °C, and the reaction time was 4 h, high‐density ZnO regular nanorods of 200 nm diameter were obtained. A possible mechanism with different synthesis methods and the influence of microwave processing are also proposed in this paper.
Well-dispersed carbon-doped ZnSn(OH) 6 submicrocubes were successfully synthesized through a facile and economical hydrothermal method at 433K, which used green chemical glucose (C 6 H 12 O 6 ) as the carbon-doping source. Photocatalytic activity of the as-synthesized C-doped ZnSn(OH) 6 was evaluated by studying photocatalytic decomposition of methylene blue (MB) in aqueous solution under visible light irradiation(ࣙ 400 nm). The results show that carbondoped ZnSn(OH) 6 photocatalysts exhibited higher photocatalytic performance as compared to pure ZnSn(OH) 6 . 1.0 wt% C-doped ZnSn(OH) 6 photocatalyst exhibited obviously higher photocatalytic activity that of pure ZnSn(OH) 6 or other C-ZnSn(OH) 6 catalysts under the same condition. The enhanced photocatalytic degradation of MB could be attributed to the doping of carbon and the possible mechanism for high photocatalytic activity of C-doped ZnSn(OH) 6 was discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.