THE recent synthesis of silica-based mesoporous materials by the cooperative assembly of periodic inorganic and surfactant-based structures has attracted great interest because it extends the range of molecular-sieve materials into the very-large-pore regime. If the synthetic approach can be generalized to transition-metal oxide mesostructures, the resulting nanocomposite materials might find applications in electrochromic or solid-electrolyte devices, as high-surface-area redox catalysts and as substrates for biochemical separations. We have proposed recently6 that the matching of charge density at the surfactant/inorganic interfaces governs the assembly process; such co-organization of organic and inorganic phases is thought to be a key aspect of biomineralization. Here we report a generalized approach to the synthesis of periodic mesophases of metal oxides and cationic or anionic surfactants under a range of pH conditions. We suggest that the assembly process is controlled by electrostatic complementarity between the inorganic ions in solution, the charged surfactant head groups and—when these charges both have the same sign—inorganic counterions. We identify a number of different general strategies for obtaining a variety of ordered composite materials

The organization of cationic or anionic organic and inorganic molecular species to produce three-dimensional periodic biphase arrays is described. The approach uses cooperative nucleation of molecular inorganic solution species with surfactant molecules and their assembly at low temperatures into liquid-crystal-like arrays. The organic/inorganic interface chemistry makes use of four synthesis routes with (S+I-), (S-I+), (S+X-I+), and (S-M+I-) direct and mediated combinations of surfactant (cationic S+, anionic S-) and soluble inorganic (cationic I+, anionic I-) molecular species. The concepts can be widely applied to generate inorganic oxide, phosphate or sulfide framework compositions. Distinct lamellar, cubic silica mesophases were synthesized in a concentrated acidic medium (S+X-I+), with the hexagonal and the cubic phases showing good thermal stability. For the hexagonal mesostructured silica materials high BET surface areas (>1000 m₂/g) are found. Hexagonal tungsten(V1) oxide materials were prepared in the presence of quaternary ammonium surfactants in the pH range 4-8. Cubic (Ia3d) and hexagonal antimony(V) oxides were obtained by acidifying (pH = 6-7) homogeneous solutions of soluble Sb(V) anions and quaternary ammonium surfactants at room temperature (S+I-). Using anionic surfactants, hexagonal and lamellar lead oxide mesostructures were found (S-I+). Crystalline zinc phosphate lamellar phases were obtained at low synthesis temperatures (4°C) and lamellar sulfide phases could be also readily generated at room temperature. The synthesis procedure presented is relevant to the coorganization of organic and inorganic phases in biomineralization processes, and some of the biomimetic implications are discussed

No abstract

KxRb1−xTiOPO4, a new nonlinear optical material with coefficients comparable to BaNa2Nb5O15, has been prepared as optically perfect single crystals which are transparent from 350 to 4500 nm. We have shown that the material is phase matchable over its entire transparency range and that 1060-nm radiation can be doubled with minimal beam walk-off. The material is free from optical damage for power densities at least as large as 150 MW/cm2. Also, it is chemically stable and easily polished.