Lignocellulose represents a key sustainable source of biomass for transformation into biofuels and bio-based products. Unfortunately, lignocellulosic biomass is highly recalcitrant to biotransformation, both microbial and enzymatic, which limits its use and prevents economically viable conversion into value-added products. As a result, effective pretreatment strategies are necessary, which invariably involves high energy processing or results in the degradation of key components of lignocellulose. In this work, the ionic liquid, 1-ethyl-3-methylimidazolium acetate ([Emim][CH 3 COO]), was used as a pretreatment solvent to extract lignin from wood flour. The cellulose in the pretreated wood flour becomes far less crystalline without undergoing solubilization. When 40% of the lignin was removed, the cellulose crystallinity index dropped below 45, resulting in >90% of the cellulose in wood flour to be hydrolyzed by Trichoderma viride cellulase. [Emim] [CH 3 COO] was easily reused, thereby resulting in a highly concentrated solution of chemically unmodified lignin, which may serve as a valuable source of a polyaromatic material as a value-added product.
Room temperature ionic liquids (RTILs) are emerging as attractive and green solvents for lignocellulosic biomass pretreatment. The unique solvating properties of RTILs foster the disruption of the 3D network structure of lignin, cellulose, and hemicellulose, which allows high yields of fermentable sugars to be produced in subsequent enzymatic hydrolysis. In the current review, we summarize the physicochemical properties of RTILs that make them effective solvents for lignocellulose pretreatment including mechanisms of interaction between lignocellulosic biomass subcomponents and RTILs. We also highlight several recent strategies that exploit RTILs and generate high yields of fermentable sugars suitable for downstream biofuel production, and address new opportunities for use of lignocellulosic components, including lignin. Finally, we address some of the challenges that remain before large-scale use of RTILs may be achieved.
Ionic liquids (ILs) have emerged as attractive solvents for lignocellulosic biomass pretreatment in the production of biofuels and chemical feedstocks. However, the high cost of ILs is a key deterrent to their practical application. Here, we show that acetate based ILs are effective in dramatically reducing the recalcitrance of corn stover toward enzymatic polysaccharide hydrolysis even at loadings of biomass as high as 50% by weight. Under these conditions, the IL serves more as a pretreatment additive rather than a true solvent. Pretreatment of corn stover with 1-ethyl-3-methylimidizolium acetate ([Emim] [OAc]) at 125 ± 5°C for 1 h resulted in a dramatic reduction of cellulose crystallinity (up to 52%) and extraction of lignin (up to 44%). Enzymatic hydrolysis of the IL-treated biomass was performed with a common commercial cellulase/xylanase from Trichoderma reesei and a commercial β-glucosidase, and resulted in fermentable sugar yields of ∼80% for glucose and ∼50% for xylose at corn stover loadings up to 33% (w/w) and 55% and 34% for glucose and xylose, respectively, at 50% (w/w) biomass loading. Similar results were observed for the IL-facilitated pretreatment of switchgrass, poplar, and the highly recalcitrant hardwood, maple. At 4.8% (w/w) corn stover, [Emim][OAc] can be readily reused up to 10 times without removal of extracted components, such as lignin, with no effect on subsequent fermentable sugar yields. A significant reduction in the amount of IL combined with facile recycling has the potential to enable ILs to be used in large-scale biomass pretreatment.
A core-sheath of multi-walled carbon nanotube (MWNT)-cellulose fibers of diameters from several hundreds nm to several µm were prepared by co-axial electrospinning from a non-valatile, non-flammable ionic liquid (IL) solvent, 1-methyl-3-methylimidazolium acetate ([EMIM][Ac]). MWNTs were dispersed in IL to form a gel solution. This gel core solution was electrospun surrounded by a sheath solution of cellulose disolved in the same IL. Electrospun fibers were collected in a coagulation bath containing ethanol-water to completely remove the IL and dried to form a core-sheath MWNT-cellulose fibers having a cable structure with a conductive core and insulating sheath. Enzymatic treatment of a portion of a mat of these fibers with cellulase selectively removed the cellulose sheath exposing the MWNT core for connection to an electrode. These MWNT-cellulose fiber mats demonstrated excellent conductivity due to a conductive pathway of bundleled MWNTs. Fiber mat conductivity increased with increasing ratio of MWNT in the fibers with a maximum conductivity of 10.7 S/m obtained at 45 wt% MWNT loading.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.