Polyfurfuryl alcohol (PFA) is one of the most intriguing polymers because, despite its easy polymerization in acid environment, its molecular structure is definitely not obvious. Many studies have been performed in recent decades, and every time, surprising aspects came out. With the present study, we aim to take advantage of all of the findings of previous investigations and exploit them for the interpretation of the completely cured PFA spectra registered with three of the most powerful techniques for the characterization of solid, insoluble polymers: Solid-State 13C-NMR, Attenuated Total Reflectance (ATR), Fourier Transform Infrared (FTIR) spectroscopy, and UV-resonant Raman spectroscopy at different excitation wavelengths, using both an UV laser source and UV synchrotron radiation. In addition, the foreseen structures were modeled and the corresponding 13C-NMR and FTIR spectra were simulated with first-principles and semi-empiric methods to evaluate their matching with experimental ones. Thanks to this multi-technique approach, based on complementary analytical tools and computational support, it was possible to conclude that, in addition to the major linear unconjugated polymerization, the PFA structure consists of Diels-Alder rearrangements occurring after the opening of some furanic units, while the terminal moieties of the chain involves γ-lactone arrangements. The occurrence of head-head methylene ether bridges and free hydroxyl groups (from unreacted furfuryl alcohol, FA, or terminal chains) could be excluded, while the conjugated systems could be considered rather limited.

Tannin foams are green lightweight materials that have attracted industrial interest for the manufacturing of sandwich panels for insulation purposes. However, the dimensions of the cells and the presence of sulfur in the formulation developed until now have discouraged their upscaling. In this work, we present the synthesis and the characterization of the more promising small cell and sulfur-free materials. It was observed that, with respect to standard ones, foams catalyzed with nitric acid present similar physical properties and more phenolic character, which favors the absorption of ionic pollutants. Conversely, the foams blown with aliphatic solvents and surfactants present smaller pores, and higher mechanical and insulating properties, without affecting the chemical properties or the heating value. The combined foam produced with nitric acid as a catalyst and petroleum ether as a blowing agent result in sulfur-free and small cell material with overall improved features. These foams have been produced at 30 × 30 × 3 cm3, with high homogeneity and, to date, they represent the most suitable formulation for industrial upscaling.

The aim of this study was to investigate the flammability of ecologically friendly, 100% natural larch and poplar bark-based panels bonded with clay. The clay acted as a fire retardant, and it improved the fire resistance of the boards by 12–15% for the surface and 27–39% for the edge of the testing specimens. The thermal conductivity was also analyzed. Although the panels had a density ranging from 600 to 900 kg/m3, thermal conductivity for the panel with a density of 600 kg/m3 was excellent, and it was comparable to lightweight insulation panels with much lower densities. Besides that, the advantage of the bark clay boards, as an insulation material, is mostly in an accumulative capacity similar to wood cement boards, and it can significantly improve the climatic stability of indoor spaces that have low ventilation rates. Bark boards with clay, similar to wood cement composites (wood wool cement composites and wood particle cement composites), have low mechanical properties and elasticity. Therefore, there their use is limited to non-structural paneling applications. These ecologically friendly, 100% natural and recyclable composites can be mostly used with respect to their thermal insulation, acoustics and fire resistance properties.

No abstract

No abstract