Solid polymer electrolyte electrochemical energy conversion devices that operate under highly alkaline conditions afford faster reaction kinetics and the deployment of inexpensive electrocatalysts compared with their acidic counterparts. The hydroxide anion exchange polymer is a key component of any solid polymer electrolyte device that operates under alkaline conditions. However, durable hydroxide-conducting polymer electrolytes in highly caustic media have proved elusive, because polymers bearing cations are inherently unstable under highly caustic conditions. Here we report a systematic investigation of novel arylimidazolium and bis-arylimidazolium compounds that lead to the rationale design of robust, sterically protected poly(arylimidazolium) hydroxide anion exchange polymers that possess a combination of high ion-exchange capacity and exceptional stability.
We report the synthesis and molecular characterization of structurally defined, sulfo-phenylated, oligo- and polyphenylenes that incorporate a novel tetra-sulfonic acid bistetracyclone monomer. The utility of this monomer in the [4 + 2] Diels-Alder cycloaddition to produce well-defined, sulfonated oligophenylenes and pre-functionalized polyphenylene homopolymers is demonstrated. Characterization of the oligophenylenes indicates formation of the meta-meta and para-para adducts in a ∼ 1:1 ratio. These functionalized monomers and their subsequent coupling provide a route to prepare novel, sterically encumbered, sulfonated polyphenylenes possessing unprecedented structural control.
Two classes of novel sulfonated phenylated polyphenylene ionomers are investigated as polyaromatic-based proton exchange membranes. Both types of ionomer possess high ion exchange capacities yet are insoluble in water at elevated temperatures. They exhibit high proton conductivity under both fully hydrated conditions and reduced relative humidity, and are markedly resilient to free radical attack. Fuel cells constructed with membrane-electrode assemblies containing each ionomer membrane yield high in situ proton conductivity and peak power densities that are greater than obtained using Nafion reference membranes. In situ chemical stability accelerated stress tests reveal that this class of the polyaromatic membranes allow significantly lower gas crossover and lower rates of degradation than Nafion benchmark systems. These results point to a promising future for molecularly designed sulfonated phenylated polyphenylenes as proton-conducting media in electrochemical technologies.
We report on poly(arylene-imidazoliums), which were synthesized by microwave polycondensation of dialdehyde with bisbenzil and quantitatively functionalized by alkylation. This cationic polyelectrolyte is sterically protected around the C2-position and is stable in 10 M KOH aq at 100 °C (t 1/2 of >5000 h). Alkaline stability is rationalized through analyses of model compounds, single crystal X-ray diffraction, and density functional theory. The polyelectrolytes form tough, pliable, transparent, ionically conductive films.
The copolymerization of a prefunctionalized, tetrasulfonated oligophenylene monomer was investigated. The corresponding physical and electrochemical properties of the polymers were tuned by varying the ratio of hydrophobic to hydrophilic units within the polymers. Membranes prepared from these polymers possessed ion exchange capacities ranging from 1.86 to 3.50 meq g−1 and exhibited proton conductivities of up to 338 mS cm−1 (80 °C, 95 % relative humidity). Small‐angle X‐ray scattering and small‐angle neutron scattering were used to elucidate the effect of the monomer ratios on the polymer morphology. The utility of these materials as low gas crossover, highly conductive membranes was demonstrated in fuel cell devices. Gas crossover currents through the membranes of as low as 4 % (0.16±0.03 mA cm−2) for a perfluorosulfonic acid reference membrane were demonstrated. As ionomers in the catalyst layer, the copolymers yielded highly active porous electrodes and overcame kinetic losses typically observed for hydrocarbon‐based catalyst layers. Fully hydrocarbon, nonfluorous, solid polymer electrolyte fuel cells are demonstrated with peak power densities of 770 mW cm−2 with oxygen and 456 mW cm−2 with air.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.