The all-vanadium redox flow battery (VRFB) is one of the most promising energy storage systems to be associated with the grid. The system has been developed for almost 30 years. A key component for VRFBs is the membrane separator, which separates the positive and negative half-cells and prevents the cross-mixing of vanadium ions, while providing required ionic conductivity. In general, research is to solve a multi-variable problem which requires optimization in both physical characteristics and electrochemical performance of the 10 membrane. Nafion and its derivatives are still important materials thanks to their high chemical stability and ionic conductivity. However, weaknesses of these materials, such as high vanadium ion crossover and high cost, stimulate new approaches in materials design for VRFBs. New achievements in material sciences and polymer chemistry allow further development of other types of polymeric materials and composites as separators in VRFBs. This includes new cation exchange membranes, anion exchange membranes, amphoteric 15 ion-exchange membranes, and non-ionic porous materials. Each type of material exhibits its advantages, accompanying with its weaknesses. Recent articles in polymer-containing membranes for use as separators in VRFBs are reviewed.Journal Name, [year], [vol], 00-00 | 5 vanadium crossover in s-Radel in comparison with that in Nafion.

The chemistry, methods, and results of corrosion studies on zinc coating using polymer-containing materials may be exploited in the development of the next generations of hybrid rechargeable aqueous batteries.

The Zn anode in secondary aqueous batteries suffers from dendrite formation and corrosion. In this work, dendrite formation was suppressed by using a simple but new gel electrolyte containing fumed silica and an additive. The dendrite suppression was evidenced by chronoamperometry and ex situ scanning electron microscopy examinations. Pyrazole was implemented as the additive in the electrolyte. It was found that the presence of 0.2 wt % pyrazole in the electrolyte helped minimize both corrosion and dendrite formation. The Zn/LiMn O battery using pyrazole-containing gel electrolytes exhibited high cyclability up to 85 % capacity retention after 500 charge-discharge cycles at 4C. This was 8 % higher than the performance of the reference battery (using aqueous electrolyte containing 2 m Li SO and 1 m ZnSO ). Furthermore, self-discharge of the battery with the pyrazole-containing gel electrolyte was suppressed, as evidenced by an open-circuit voltage loss that was 20 % lower than for the reference battery after 24 h monitoring. Float-charge current density under constant voltage (2.1 V) also significantly decreased from approximately 8.0 to 3-6 μA.

No abstract

A rechargeable hybrid aqueous battery (ReHAB) containing NASICON-type M3V2(PO4)3 (M = Li, Na) as the cathodes and Zinc metal as the anode, working in Li2SO4-ZnSO4 aqueous electrolyte, has been studied. Both of Li3V2(PO4)3 and Na3V2(PO4)3 cathodes can be reversibly charge/discharge with the initial discharge capacity of 128 mAh g−1 and 96 mAh g−1 at 0.2C, respectively, with high up to 84% of capacity retention ratio after 200 cycles. The electrochemical assisted ex-XRD confirm that Li3V2(PO4)3 and Na3V2(PO4)3 are relative stable in aqueous electrolyte, and Na3V2(PO4)3 showed more complicated electrochemical mechanism due to the co-insertion of Li+ and Na+. The effect of pH of aqueous electrolyte and the dendrite of Zn on the cycling performance of as designed MVP/Zn ReHABs were investigated, and weak acidic aqueous electrolyte with pH around 4.0–4.5 was optimized. The float current test confirmed that the designed batteries are stable in aqueous electrolytes. The MVP//Zn ReHABs could be a potential candidate for future rechargeable aqueous battery due to their high safety, fast dynamic speed and adaptable electrochemical window. Moreover, this hybrid battery broadens the scope of battery material research from single-ion-involving to double-ions -involving rechargeable batteries.

No abstract

No abstract

No abstract