The possibility of crystallization of ZSM-5 with high Si/Al ratio was evaluated through the combined use of crystallization seeds and organic compounds that are not conventional directing agents for ZSM-5 (ethanol, methylamine, ethylamine, propylamine, butylamine, isopropylamine and diethylamine) in order to find a less toxic and costly route of synthesis. In addition, the influence of the stirring during the crystallization step on the properties of the ZSM-5 obtained in these synthesis conditions was verified. The obtained zeolites were analyzed by X-ray diffractometry in order to understand the effects of the templates. The analyses of NH3-TPD, nitrogen adsorption, SEM, and TG/DTA were performed for the samples with better crystallinity. The procedure was successfully employed for the synthesis of MFI samples using propylamine as an alternative structure-directing agent. Its mean crystallite size ranged from 23 to 24 nm and was efficient in the cracking reaction of n-hexane.
As zeólitas apresentam significativa importância econômica para a indústria química e petroquímica. Desde o início do seu uso (1954) como catalisador e/ou peneira molecular vem mostrando crescente aplicação no refino do petróleo, com ênfase no craqueamento. A zeólita ZSM-22, embora eficiente para determinadas reações, ainda não é objeto de muitos estudos quando comparada com zeólitas em uso comercial. Uma etapa crucial para a viabilidade comercial da ZSM-22 é o processo de síntese que, em geral, utiliza direcionadores de estrutura e tempos de cristalização longos, tornando o material oneroso. Este trabalho pretende destacar a importância do desenvolvimento de rotas para obtenção da ZSM-22, visto seu potencial de aplicação. Para tanto, se desenvolve uma fundamentação teórica a partir de patentes e artigos acessíveis nas bases de dados do INPI, Espacenet, WIPO, DERWENT e USPTO e Periódicos Capes. Como resultado desta análise, foram estabelecidos as tendências e problemas para obtenção da ZSM-22.Palavras chave: Zeólita. ZSM-22. Sementes.
A síntese das amostras de mordenita foram realizadas através do método hidrotérmico, utilizando dois tipos diferentes de sementes de cristalização (mordenita e ferrierita), onde foram explorados a variação de alguns parâmetros de síntese, como a razão SiO2/Al2O3 = 20, 60 e 100, e a razão OH/SiO2= 0,2, 0,3 e 0,4, em diferentes tempos de cristalização, à temperatura de 170 °C. As amostras foram caracterizadas por difratometria de raios X (DRX), análises termogravimétricas (ATG), adsorção de nitrogênio a -196 °C (BET) e dessorção à temperatura programada de amônia (DTP-NH3). Constatou-se que a utilização da razão OH/SiO2 = 0,4, em conjunto com as sementes de MOR e FER foram obtidas as amostras mais cristalinas, evidenciando o papel crucial do agente mineralizante OH- no meio.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.