A freestanding GaN substrate over 2 inches in size was successfully prepared for the first time by hydride vapor phase epitaxy (HVPE) using GaAs as a starting substrate. In the experiment, a GaAs (111)A substrate with a SiO 2 mask pattern on its surface was used. A thick GaN layer was grown on the GaAs substrate at 1030 • C through the openings in the SiO 2 mask. By dissolving the GaAs substrate in aqua regia, a freestanding GaN substrate about 500 µm thick was obtained. The fullwidth at half maximum (FWHM) in the ω-mode X-ray diffraction (XRD) profile of GaN (0002) plane was 106 arcsec. The dislocation density of the GaN substrate obtained was determined to be as low as 2 × 10 5 cm −2 by plan-view transmission electron microscopy (TEM). Hall measurements revealed the n-type conductivity of the GaN substrate with typical carrier concentration and carrier mobility of 5 × 10 18 cm −3 and 170 cm 2 ·V −1 ·s −1 , respectively.
BioOne Complete (complete.BioOne.org) is a full-text database of 200 subscribed and open-access titles in the biological, ecological, and environmental sciences published by nonprofit societies, associations, museums, institutions, and presses.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.