No abstract

PURPOSEThe purpose of this study was to evaluate and compare the effects of different surface pretreatment techniques on the surface roughness and shear bond strength of a new self-adhering flowable composite resin for use with lithium disilicate-reinforced CAD/CAM ceramic material.MATERIALS AND METHODSA total of one hundred thirty lithium disilicate CAD/CAM ceramic plates with dimensions of 6 mm × 4 mm and 3 mm thick were prepared. Specimens were then assigned into five groups (n=26) as follows: untreated control, coating with 30 µm silica oxide particles (Cojet™ Sand), 9.6% hydrofluoric acid etching, Er:YAG laser irradiation, and grinding with a high-speed fine diamond bur. A self-adhering flowable composite resin (Vertise Flow) was applied onto the pre-treated ceramic plates using the Ultradent shear bond Teflon mold system. Surface roughness was measured by atomic force microscopy. Shear bond strength test were performed using a universal testing machine at a crosshead speed of 1 mm/min. Surface roughness data were analyzed by one-way ANOVA and the Tukey HSD tests. Shear bond strength test values were analyzed by Kruskal-Wallis and Mann-Whitney U tests at α=.05.RESULTSHydrofluoric acid etching and grinding with high-speed fine diamond bur produced significantly higher surface roughness than the other pretreatment groups (P<.05). Hydrofluoric acid etching and silica coating yielded the highest shear bond strength values (P<.001).CONCLUSIONSelf-adhering flowable composite resin used as repair composite resin exhibited very low bond strength irrespective of the surface pretreatments used.

No abstract

Objective: To evaluate the effect of cavity disinfectants on the immediate microtensile bond strength (μTBS) of an etch-and-rinse adhesive to water-and ethanolsaturated sound and caries-affected dentin (CAD). Material and Methods: Thirty-six human molars were sectioned to expose 1/3 of the mid-coronal dentin surface. Sound (n = 18) and CAD (n = 18) specimens were divided into six groups each (n = 3): one positive control (sound), one negative control (CAD), and five experimental groups each. In the control group, dentin surfaces were bonded using an etch-and-rinse adhesive with a traditional water-wet bonding technique. In the experimental groups, ozone was applied before etching and chlorhexidine after etching. In the ethanol-wet bonding groups, acid-etched dentin surfaces were treated with ethanol. Following adhesive application and composite buildups, bonded specimens were sectioned to form sticks. Failure modes were analyzed using a stereomicroscope. Results: The water-wet bonded sound control group yielded the highest μTBS among all groups (p < 0.001). The lowest μTBS values were observed in the ozone groups (p < 0.05). The ethanol-wet bonded CAD group exhibited a higher μTBS than the water-wet bonded negative controls. Although compared to the positive control, chlorhexidine decreased the μTBS (p < 0.05), an increase with no significant difference was observed in the negative control (p > 0.05). Conclusions:The μTBS values of CAD were lower than those of sound dentin. Ethanol-wet bonding improved the μTBS of CAD. Ozone application reduced the μTBS in both sound and CAD; chlorhexidine improved the immediate μTBS after etching in CAD.

Purpose:This study investigated the influence of sealant application on stain resistance of a nanohybrid resin composite compared to the efficacy of a bonding agent used as a surface sealant on prolonging color stability of the resin composite.Materials and Methods:28 disc-shaped materials were prepared from a nano-hybrid resin composite Filtek Z550 and assigned to four groups: G1K: nonsealed; G2:Adper Single Bond; G3: Fortify ; G4: Biscover LV. After 24 h storage in distilled water at 37˚C, all specimens were subjected to thermocycling and immersed into coffee solution. Color measurements were performed using spectrophotometer (VITA Easyshade; Vident) according to CIEL*a*b* system.Results:Color change values were significantly different among the groups in each evaluation period except for after thermocycling (p<0.05). For 7 days evaluation period, the difference between G3 and G4 group was statistically significant while G4 exhibited statistically significant differences (p<0.05 and p<0.0001 respectively) compared to control (G1) in 14 day whereas no significant difference was found between GI and GII in 28-day evaluation period. However, ΔE values of sealed specimens (GIII, GIV) differed significantly from non-sealed (GI) specimens after 28 days of immersion in coffee solution (p<0.05 and p<0.0001 respectively).Conclusion:It may be concluded that using a bonding agent as a surface sealant does not increase stain resistance of resin composites of the sealants evaluated. Biscover LV showed the highest efficacy to prolong color stability of the resin composite.

No abstract

No abstract

Purpose of this in situ study was to evaluate the surface properties of eroded dentin specimens activated with three different matrix metalloproteinase (MMP) inhibitors (chlorhexidine [CHX], fluoride, green tea), black tea, and water. One hundred eighty dentin samples were prepared from extracted third molars and then samples divided into six groups. Ten volunteers were carried three specimens of each group, on acrylic palatal appliances, which were fabricated exactly for them (n = 3). Erosive cycles were done by immersing appliances in cup containing Cola and was followed by rinsing with test solutions. Microhardness values were measured. Surface properties were investigated by atomic force microscopy (AFM). Lowest change in microhardness was shown in fluoride group whereas negative control group (water) had the highest change. There were no statistically significant differences among surface roughness changes (p > .05). The least change in microhardness was seen in the fluoride group (13.05 ± 8.07), while the control group showed the highest change (33.80 ± 12.42) and was statistically significant when compared to other groups (p < .05). Besides lowest depth, values were shown in fluoride group as well. AFM evaluations showed macromolecular deposits on surfaces of fluoride, CHX, and black tea groups. No superior results were detected in CHX + fluoride group and black tea showed similar surface characteristics as green tea. Mouthrinses containing not only green tea but also black tea could be beneficial for patients with exposed dentin surfaces. Catechines and theaflavins in teas could be useful for improving surface quality.