Oxygen vacancies (V O s) in ZnO are well-known to enhance photocatalytic activity (PCA) despite various other intrinsic crystal defects. In this study, we aim to elucidate the effect of zinc interstitials (Zn i ) and V O s on PCA, which has applied as well as fundamental interest. To achieve this, the major hurdle of fabricating ZnO with controlled defect density requires to be overcome, where it is acknowledged that defect level control in ZnO is significantly difficult. In the present context, we fabricated nanostructures and thoroughly characterized their morphological (SEM, TEM), structural (XRD, TEM), chemical (XPS) and optical (photoluminescence, PL) properties. To fabricate the nanostructures, we adopted atomic layer deposition (ALD), which is a powerful bottom-up approach. However, to control defects, we chose polysulfone electrospun nanofibers as a substrate on which the non-uniform adsorption of ALD precursors is inevitable because of the differences in the hydrophilic nature of the functional groups. For the first 100 cycles, Zn i s were predominant in ZnO quantum dots (QDs), while the presence of V O s was negligible. As the ALD cycle number increased, V O s were introduced, whereas the density of Zn i remained unchanged. We employed PL spectra to identify and quantify the density of each defect for all the samples. PCA was performed on all the samples, and the percent change in the decay constant for each sample was juxtaposed with the relative densities of Zn i s and V O s. A logical comparison of the relative defect densities of Zn i s and V O s suggested that the former are less efficient than the latter because of the differences in the intrinsic nature and the physical accessibility of the defects. Other reasons for the efficiency differences were elaborated.
High molecular weight polymers and high polymer concentrations are desirable for the electrospinning of nanofibers since polymer chain entanglements and overlapping are important for uniform fiber formation. Hence, the electrospinning of nanofibers from non-polymeric systems such as cyclodextrins (CDs) is quite a challenge since CDs are cyclic oligosaccharides. Nevertheless, in this study, we have successfully achieved the electrospinning of nanofibers from chemically modified CDs without using a carrier polymer matrix. Polymer-free nanofibers were electrospun from three different CD derivatives, hydroxypropyl-β-cyclodextrin (HPβCD), hydroxypropyl-γ-cyclodextrin (HPγCD) and methyl-β-cyclodextrin (MβCD) in three different solvent systems, water, dimethylformamide (DMF) and dimethylacetamide (DMAc). We observed that the electrospinning of these CDs is quite similar to polymeric systems in which the solvent type, the solution concentration and the solution conductivity are some of the key factors for obtaining uniform nanofibers. Dynamic light scattering (DLS) measurements indicated that the presence of considerable CD aggregates and the very high solution viscosity were playing a key role for attaining nanofibers from CD derivatives without the use of any polymeric carrier. The electrospinning of CD solutions containing urea yielded no fibers but only beads or splashes since urea caused a notable destruction of the self-associated CD aggregates in their concentrated solutions. The structural, thermal and mechanical characteristics of the CD nanofibers were also investigated. Although the CD derivatives are amorphous small molecules, interestingly, we observed that these electrospun CD nanofibers/nanowebs have shown some mechanical integrity by which they can be easily handled and folded as a free standing material.
Heterojunctions are a well-studied material combination in photocatalysis studies, the majority of which aim to improve the efficacy of the catalysts. Developing novel catalysts begs the question of which photo-generated charge carrier is more efficient in the process of catalysis and the associated mechanism. To address this issue we have fabricated core-shell heterojunction (CSHJ) nanofibers from ZnO and TiO 2 in two combinations where only the 'shell' part of the heterojunction is exposed to the environment to participate in the photocatalysis. Core and shell structures were fabricated via electrospinning and atomic layer deposition, respectively which were then subjected to calcination. These CSHJs were characterized and studied for photocatalytic activity (PCA). These two combinations expose electrons or holes selectively to the environment. Under suitable illumination of the ZnO-TiO 2 CSHJ, e/h pairs are created mainly in TiO 2 and the electrons take part in catalysis (i.e. reduce the organic dye) at the conduction band or oxygen vacancy sites of the 'shell', while holes migrate to the core of the structure. Conversely, holes take part in catalysis and electrons diffuse to the core in the case of a TiO 2 -ZnO CSHJ. The results further revealed that the TiO 2 -ZnO CSHJ shows $1.6 times faster PCA when compared to the ZnO-TiO 2 CSHJ because of efficient hole capture by oxygen vacancies, and the lower mobility of holes.
We produced functional nanowebs, containing vanillin, having prolonged shelf-life and high temperature stability facilitated by cyclodextrin (CD) inclusion complexation. Polyvinyl alcohol (PVA) nanowebs incorporating vanillin/cyclodextrin inclusion complex (vanillin/CD-IC) were produced via electrospinning technique. The vanillin/CD-IC was prepared with three types of CDs; α-CD, β-CD and γ-CD to find out the most favourable CD type for the stabilization of vanillin. PVA/vanillin/CD-IC nanofibres, having fibre diameters around ∼200 nm, were successfully electrospun from aqueous mixture of PVA and vanillin/CD-IC. Our results indicated that vanillin with enhanced durability and high temperature stability was achieved for PVA/vanillin/CD-IC nanowebs due to complexation of vanillin with CD, whereas the PVA nanofibres without CD-IC could not effectively preserve the vanillin. Additionally, we observed that PVA/vanillin/γ-CD-IC nanoweb was more effective for the stabilization and slow release of vanillin suggesting that the strength of interaction between vanillin and the γ-CD cavity is stronger when compared to α-CD and β-CD. © 2012 Elsevier Ltd. All rights reserved
We report on the synthesis and photocatalytic activity (PCA) of electrospun poly(acrylonitrile) (PAN) nanofibrous mat decorated with nanoneedles of zinc oxide (ZnO). Apart from a detailed morphological and structural characterization, the PCA has been carefully monitored and the results are discussed elaborately when juxtaposed with the photoluminescence. The present hierarchal homoassembled nanostructures are a combination of two types of ZnO with diverse optical qualities, i.e. (a) controlled deposition of ZnO coating on nanofibers with dominant oxygen vacancies and significant grain boundaries by atomic layer deposition (ALD), and (b) growth of single crystalline ZnO nanoneedles with high optical quality on the ALD seeds via hydrothermal process. The needle structure (~25. nm in diameter with an aspect ratio of ~24) also supports the vectorial transport of photo-charge carriers, which is crucial for high catalytic activity. Furthermore, it is shown that enhanced PCA is because of the catalytic activity at surface defects (on ALD seed), valence band, and conduction band (of ZnO nanoneedles). PCA and durability of the PAN/ZnO nanofibrous mat have also been tested with aqueous solution of methylene blue and the results showed almost no decay in the catalytic activity of this material when reused. © 2014 Elsevier B.V
We have demonstrated that cyclodextrin (CD) (a non-polymeric system) can be electrospun into nanofibers by itself; methyl-beta-cyclodextrin (MbetaCD) nanofibers were electrospun and it was observed that the success of the electrospinning of the CD nanofibers strongly depends on (i) type of solvent, (ii) CD solution concentration and (iii) intermolecular interactions between the CD molecules.
Polymer−inorganic core−shell nanofibers were produced by two-step approach; electrospinning and atomic layer deposition (ALD). First, nylon 6,6 (polymeric core) nanofibers were obtained by electrospinning, and then zinc oxide (ZnO) (inorganic shell) with precise thickness control was deposited onto electrospun nylon 6,6 nanofibers using ALD technique. The bead-free and uniform nylon 6,6 nanofibers having different average fiber diameters (∼80, ∼240 and ∼650 nm) were achieved by using two different solvent systems and polymer concentrations. ZnO layer about 90 nm, having uniform thickness around the fiber structure, was successfully deposited onto the nylon 6,6 nanofibers. Because of the low deposition temperature utilized (200°C ), ALD process did not deform the polymeric fiber structure, and highly conformal ZnO layer with precise thickness and composition over a large scale were accomplished regardless of the differences in fiber diameters. ZnO shell layer was found to have a polycrystalline nature with hexagonal wurtzite structure. The core−shell nylon 6,6-ZnO nanofiber mats were flexible because of the polymeric core component. Photocatalytic activity of the core−shell nylon 6,6-ZnO nanofiber mats were tested by following the photocatalytic decomposition of rhodamine-B dye. The nylon 6,6-ZnO nanofiber mat, having thinner fiber diameter, has shown better photocatalytic efficiency due to higher surface area of this sample. These nylon 6,6-ZnO nanofiber mats have also shown structural stability and kept their photocatalytic activity for the second cycle test. Our findings suggest that core−shell nylon 6,6-ZnO nanofiber mat can be a very good candidate as a filter material for water purification and organic waste treatment because of their photocatalytic properties along with structural flexibility and stability. KEYWORDS: electrospinning, ALD (atomic layer deposition), nanofibers, ZnO, core−shell, photocatalytic activity, nylon ■ INTRODUCTIONOne-dimensional (1D) nanostructures such as nanofibers have distinctive properties that can offer good opportunities for developing advanced materials and devices.1−3 Among the other nanofiber fabrication methods, electrospinning has gained growing interest in the past decade because this technique is quite versatile and cost-effective for producing functional nanofibers from variety of materials including polymers, polymer blends, emulsions, suspensions, sol−gels, metal oxides, composite structures as well as nonpolymeric systems, etc. 2−8Electrospun nanofibers and their nanofiber mats have remarkable characteristics including a very high specific surface area, pore sizes within the nanoscale and very lightweight since the fiber diameter ranges from one micrometer down to a few tens of nanometers. Moreover, the control of the fiber surface morphology, fiber orientation, and cross-sectional configuration, and design flexibility for physical/chemical modification is quite feasible for obtaining multifunctional electrospun nanofibers. Because of their exceptional pr...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.