The hot-tack properties of ethylene-methacrylic acid copolymers neutralized with sodium (Na) cations to produce ionomers were investigated. Specimens with neutralization degrees of 20%, 54%, and 70% were examined. After testing at low sealing temperatures (<130 C), the highest hot-tack strength was obtained from a specimen with a neutralization degree of 20%. In contrast, at high sealing temperatures (>140 C), the hot-tack strength increased with an increasing degree of neutralization. Observations of the surfaces of samples tested at low sealing temperatures after hot-tack tests showed that specimens having a neutralization degree of 20% exhibited cohesive breakdown while the 54% and 70% specimens underwent interfacial delamination. The effect of sealing temperature on hot-tack strength was determined by assessing the rheological properties of molten ionomers. The results suggested that, when testing at low sealing temperatures, a low melt viscosity provided high hot-tack strength by allowing flow diffusivity of the resin at the sealed interface. At high sealing temperatures, uniaxial elongational viscosity related to strain hardening contributed to the high hot-tack strength of these Na-based ionomers. The present study highlights the important effect of ionic aggregates on hot-tack properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.