The effect of thermal and shear histories on the crystallization rate of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) was studied. As with other crystalline polymers, the shear history greatly affected the crystallization rate when the shear rate was beyond a critical value, i.e., the inverse of the Rouse relaxation time. Even after the formation of extended chain crystals, spherulite texture was clearly discernable. It grew from certain points on the extended chain crystals. Consequently, a row of spherulites appeared along the flow direction. The resin temperature in the molten state was also significant. When the sample was heated to 170°C, which is beyond the main melting peak in the differential scanning calorimetry curve, unmolten crystals did not affect the linear viscoelastic properties. They acted as effective nucleating agents for the rest of the polymer during cooling. Therefore, the shear history hardly affected the crystallization rate and the number of spherulites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.