Zinc oxide and layered zinc hydroxides were deposited from an aqueous solution of zinc nitrate at 323−358 K on a substrate plate with a very thin titanium dioxide film by a photocatalytic reaction. The amorphous or low crystalline zinc hydroxide aggregates were deposited at a low temperature. The zinc oxide crystals with about 1−2 μm-sized hexagonal columns and 10 nm-sized spheres were formed at 338−358 K. Nitrate ions in the solution were reduced to nitrite ions, and water was transformed into hydroxide ions by a photocatalytic reaction on the titanium dioxide film. The pH value increased on the substrate surface with the titanium dioxide film, which caused the zinc hydroxide formation on the film.The zinc hydroxides were then dehydrated and transformed into zinc oxide. The average crystallite size of the zinc oxide decreased with an increase in the reaction temperature because the reaction rates of the formation and dehydration of the zinc hydroxides increased which resulted in an increase in the formation rate of the crystal zinc oxide nuclei.
Dye-dispersing ZnO precursor gel films were prepared on indium tin oxide electrodes from a zinc acetate solution containing eosin Y by dip-coating, steam treatment, and then heating at a low temperature. The electronic interaction between the dye and zinc in the dye-dispersing gel films were investigated by spectroscopic and electrochemical measurements. A photocurrent was observed in the dye-dispersing gel electrodes before the steam treatment. The photocurrent value increased by the steam treatment and heating due to crystallization of the gel and removal of organic impurities. The dye molecules existed between the interlayers of the layered zinc hydroxide coexisting with the ZnO. The photoexcited electron in the dye should be injected into the ZnO conduction band via the layered zinc hydroxide. The value increased with an increase in the dye content even though the ZnO crystallinity decreased.The dye-zinc interaction, i.e., the complex formation and photoinduced electron injection, played an important role in the electron transport and photoelectric conversion.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.