Hydrogen peroxide (H 2 O 2 ) generation and hydrogen oxidation reaction (HOR) properties of Ir(hkl) (hkl = 111, 100, and 110) were investigated in acidic media using scanning electrochemical microscopy. In the 0.06−0.3 V vs reversible hydrogen electrode potential region, H 2 O 2 generation properties were significantly suppressed for the Ir(hkl) surfaces in comparison with Pt(111): only the Ir(100) revealed slight evolution of H 2 O 2 at ca. 0.1 V. Conversely, the HOR activity trend of the Ir(hkl) was Ir(111) > Ir(100) > Ir(110), and the activity of Ir( 111) is approximately 70% of that of Pt(111). This study presents Ir-based nanosized catalysts whose surface comprises mainly ( 111) facets (such as octahedron-shape) as effective anode catalysts for polymer electrolyte fuel cells.
From the viewpoint of the application of Ir-Ru alloys for anode of proton exchange membrane fuel cells (PEMFCs), hydrogen peroxide (H2O2) generation and the hydrogen oxidation reaction (HOR) properties of...
Simultaneous accomplishment of high hydrogen oxidation reaction (HOR) activity and suppressed hydrogen peroxide (H2O2) generation is desired for anode catalysts of polymer electrolyte fuel cells. 0.3 monolayer-thick-Pt-deposited Ir(111) showed threefold...
High-entropy alloys (HEAs) have attracted considerable attention to improve performance of various electrocatalyst materials. A comprehensive understanding of the relationship between surface atomic-level structures and catalytic properties is essential to boost the development of novel catalysts. In this study, we propose an experimental study platform that enables the vacuum synthesis of atomic-level-controlled single-crystal high-entropy alloy surfaces and evaluates their catalytic properties. The platform provides essential information that is crucial for the microstructural fundamentals of electrocatalysis, i.e., the detailed relationship between multi-component alloy surface microstructures and their catalytic properties. Nanometre-thick epitaxially stacking layers of Pt and equi-atomic-ratio Cr-Mn-Fe-Co-Ni, the so-called Cantor alloy, were synthesised on low-index single-crystal Pt substrates (Pt/Cr-Mn-Fe-Co-Ni/Pt(hkl)) as a Pt-based single-crystal alloy surface model for oxygen reduction reaction (ORR) electrocatalysis. The usefulness of the platform was demonstrated by showing the outperforming oxygen reduction reaction properties of high-entropy alloy surfaces when compared to Pt-Co binary surfaces.
Introduction Nanoparticles of Pt as well as Pt-based alloys are widely used as cathode catalyst materials for proton exchange membrane fuel cells (PEMFC). However, electrochemical stability of the materials is rather low under practical operating conditions of PEMFC cathode, resulting in severe deactivation of oxygen reduction reaction (ORR). Therefore, further material’s developments are required for next-generation PEMFC cathode catalysts, i.e., more enhanced ORR durability with low platinum group metal (PGM) usage. High entropy alloys (HEAs), defined as single phase solid solutions of five or more elements in equal composition ratios, are known as thermodynamically stable, in comparison to conventional binary alloys. Furthermore, complex atomic-level local structures bring about unique electronic as well as (electro-)chemical properties that originating from lattice strains induced by specific local structures and/or so-called sluggish diffusion of the constituent elements. [1] However, to our best knowledge, no study has been made for ORR properties of Pt alloying with non-PGM Cantor alloy (fcc structure HEA with equi-atomic ratio of Cr-Mn-Fe-Co-Ni [2]) elements in strong acid condition. In this study, we synthesized lattice stacking structures of Pt/HEA(hkl) (hkl = (111), (110), (100)) through arc-plasma deposition (APD) of the Cantor alloy layer on Pt(hkl) substrate surfaces, followed by deposition of the surface Pt layer in ~10-7 Pa. Then, we performed cross-sectional STEM-EDS observations for Pt/HEA/Pt(hkl) stacking structures with atomic-level resolution and evaluated the ORR properties (initial activity and structural stability). Experimental An APD target of Cr-Mn-Fe-Co-Ni (Cantor alloy) was fabricated by sintering of equal quantity corresponding elements. 10 ML(monolayer)-thick (1 ML = ca. 0.3 nm) Cantor alloy layer (as HEA) was vacuum-deposited by APD on surface cleaned Pt(hkl) substrate surfaces at 300 K, and subsequently annealed in vacuum at 773 K for 30 minutes. Then, 4ML-thick Pt layer was deposited on the pre-deposited Cantor alloy layer at 300 K and annealed at 623 K. The samples thus prepared are designated as Pt/HEA/Pt(hkl). The atomic-level micro-structures and chemical bonding states of Pt/HEA/Pt(hkl) surfaces were characterized by cross-sectional STEM-EDS, RHEED, XPS etc. CV and LSV with the RDE method were conducted in N2-purged and O2-saturated 0.1 M HClO4. ORR activity was evaluated from j k values at 0.9 V vs. RHE by using Koutecky-Levich equation and structural stability (ORR durability) was discussed based upon activity transitions during applying the potential cycles (PCs) of 0.6(3s)‐1.0(3s) V vs. RHE in O2 saturated 0.1 M HClO4 at room temperature. Results and Discussion Atomically-resolved, cross-sectional HAADF-STEM images for Pt/HEA/Pt(hkl) (a) and EDS line profiles of elemental distributions at corresponding yellow arrows (b) are presented in Figure 1. As clearly shown in (a), irrespective of the Pt surface indices, (hkl), HEA (Cantor alloy) and surface Pt layers are epitaxially grown on the substrates. By contrast, elemental distributions in each surface normal (b) seriously depend on the substrate Pt lattice indices. Notably, severe thermal diffusion of the constituent elements including Pt is confirmed by (a) and (b) for both Pt/HEA/Pt(110) and (100). Figure 2 summarizes electrochemical results. 4ML-thick-Pt/10ML-thick-Co/Pt(hkl) that prepared under the same preparation condition of Pt/HEA/Pt(hkl), and clean Pt(hkl) (light blue and gray, respectively) are also shown as references. As shown in the figure, the Pt/HEA and Pt/Co fabricated on Pt(111) substrate (top) show quite similar CV characteristics (shrink in hydrogen adsorption charges (0 – 0.3 V) and higher potential shifts in oxygen-related species adsorption (0.6 – 1.0 V)), in comparison to clean Pt(111), and almost the same initial ORR activity. Meanwhile, the Pt/HEA fabricated on Pt(110) and (100) substrates show more reduced hydrogen absorption charges, compared with corresponding Pt/Co samples. Particularly, distinctive redox features for clean Pt(110) at 0.12 V and for Pt(100) at 0.35 V are absent for corresponding CVs, suggesting specific topmost surface atomic-structures might be formed in the electrolyte, that probably resulting from significant electronic interactions between surface Pt and HEA constituent elements (Cr, Mn, Fe, Co, Ni) and/or local strain of the surface Pt layer induced by distorted Pt-HEA lattices located nearby. One might notice that Pt/HEA/Pt(110) reveals remarkable ORR activity enhancement compared with corresponding Pt/Co/Pt(110), while the activities for Pt/HEA and corresponding Pt/Co surfaces fabricated on Pt(100) are almost the same value. At the meeting, correlations between surface atomic-level micro-structures of Pt/HEA/Pt(hkl) and ORR properties will be discussed in detail. Acknowledgement This study was supported by new energy and industrial technology development organization (NEDO) of Japan and JST SPRING, Grant Number JPMJJSP2114. Reference [1] J. Yeh, JOM, 65, 1759 (2013). [2] B. Cantor et al., Mater. Sci. Eng. A, 375, 213 (2004). Figure 1
Introduction Hydrogen peroxide (H2O2) can be generated through oxygen reduction reaction (ORR) particularly on the anode Pt/C surface due to oxygen crossover during operation of polymer electrolyte fuel cell (PEFC): such the H2O2 generation causes degradation of PEFC through reactive radical generations which severely attack the PE.1 Therefore, development of a novel anode catalyst is crucial that less-active for the H2O2 generation and, yet, active for hydrogen oxidation reaction (HOR). According to Durst et al., HOR activity of the Ir/C was about 1/3 of that of the Pt/C,2 and furthermore, we found to date that Ir(111) generates much less H2O2 than Pt(111) in low potential (< 0.3 V).3 Therefore, Pt-Ir bimetallic alloy is expected to suppress H2O2 generation with keeping practical HOR activity. Nevertheless, to our best knowledge, neither H2O2 generation nor HOR properties of Pt-Ir bimetallic surfaces has been reported. Therefore, in this study, we prepared well-defined Pt/Ir(111) and Ir/Pt(111) surfaces and investigated the H2O2 generation and HOR activity. Experimental The Pt/Ir(111) and Ir/Pt(111) bimetallic surfaces were fabricated as follows. First, Ir(111) or Pt(111) surfaces were cleaned by repeated cycles of Ar+ sputtering and annealing at 1153 K in ultra-high vacuum (UHV). Then, 0.1 monolayer (ML)-equivalent Pt or Ir were deposited on the respective Ir(111) and Pt(111) surfaces by arc-plasma deposition (APD) at room temperature. The surface morphology was verified by scanning tunneling microscopy (STM) in UHV. The electrocatalytic properties were evaluated by scanning electrochemical microscope (SECM) using Pt microelectrode (diameter: ca. 20 μm) as a tip electrode. The H2O2 generation property was investigated in O2-saturated 0.1 M HClO4.4 The substrate potential (E S; Pt/Ir(111) or Ir/Pt(111)) was swept by 2 mV/s, and the tip current (i T) due to H2O2 detection was recorded with the constant tip potential (E T) of 1.26 V and tip-substrate distance of 50 μm. The HOR activity was evaluated in an electrolyte containing 0.01 M HClO4 and 0.1 M NaClO4 solution.5 The tip electrode was set as close as possible to the substrate, and E S was swept by 5 mV/s while E T was fixed at −0.74 V. The standard rate constants (k 0) for HOR were estimated by fitting the E S-dependent i T values to the theoretical ones, following to the previous reports.6 All potentials are referenced to that of the RHE. Results and Discussion Fig. 1 shows the UHV-STM images for the Pt/Ir(111) (a) and Ir/Pt(111) (b) surfaces. The dispersed nano-sized, particle-like structures that ascribable to the AP-deposited Pt (a) or Ir (b) can be observed with the atomic steps of the single crystal substrates. The surface area differences estimated from the images were 1.05 and 1.11 for the Pt/Ir(111) and Ir/Pt(111), respectively.The potential-dependent H2O2 generation for the corresponding surfaces are shown in Fig.2 (a) with the simultaneously recorded linear sweep voltammograms (LSVs) (b). The results for clean Ir(111) and Pt(111) are also presented...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.